“…The u values of these monolayers were calculated to be 23.8 ± 3.5°and 22.7 ± 3.7°, respectively. These values are better than those of other SAMs and similar to previous reports (17 ± 1 Å and 25-30°) [32,37]. This again indicates that a highly dense and organized C 12 SH-SAMs can be formed from EtOH-H 2 O and neat C 12 SH liquid.…”
Section: Resultssupporting
confidence: 91%
“…The average cant angle u value of this monolayer was roughly calculated using u = arccos(d/l), assuming a trans-extended hydrocarbon chain with no gauche defects, where l is the length from gold surface to the chain end of C 12 SH (20.3 Å) [31][32]; difference value of the current density at À0.2 V and 0.5 V (Di p = i p,À0.2 V À i p,0.5 V ) was obtained from cyclic voltammogram performed in 0.1 M Na 2 SO 4 containing 2 mM K 3 Fe(CN) 6 …”
“…The u values of these monolayers were calculated to be 23.8 ± 3.5°and 22.7 ± 3.7°, respectively. These values are better than those of other SAMs and similar to previous reports (17 ± 1 Å and 25-30°) [32,37]. This again indicates that a highly dense and organized C 12 SH-SAMs can be formed from EtOH-H 2 O and neat C 12 SH liquid.…”
Section: Resultssupporting
confidence: 91%
“…The average cant angle u value of this monolayer was roughly calculated using u = arccos(d/l), assuming a trans-extended hydrocarbon chain with no gauche defects, where l is the length from gold surface to the chain end of C 12 SH (20.3 Å) [31][32]; difference value of the current density at À0.2 V and 0.5 V (Di p = i p,À0.2 V À i p,0.5 V ) was obtained from cyclic voltammogram performed in 0.1 M Na 2 SO 4 containing 2 mM K 3 Fe(CN) 6 …”
“…The d value of the C 12 SH-SAM formed under ultrasonic irradiation at 100 W (0.1 W cm −2 ) for 15 min was calculated to be 17.5Å. The tilt angle ϕ value of the molecules in this monolayer was calculated to be 30 • using ϕ = 57.3 arccos(d/l), where l is the length from gold surface to the chain end of C 12 SH (20.3Å) [17,18]. These values are better than those of other SAMs and similar to previous reports (17 ± 1Å and 25 • -30 • ) [18,19].…”
Section: Performed In 01 M Na 2 So 4 Without Any Redox Speciesmentioning
confidence: 99%
“…The tilt angle ϕ value of the molecules in this monolayer was calculated to be 30 • using ϕ = 57.3 arccos(d/l), where l is the length from gold surface to the chain end of C 12 SH (20.3Å) [17,18]. These values are better than those of other SAMs and similar to previous reports (17 ± 1Å and 25 • -30 • ) [18,19]. This again indicates that a highly dense and organized C 12 SH-SAM can be formed under ultrasonic irradiation at 100 W (0.1 W cm −2 ) for 15 min.…”
Section: Performed In 01 M Na 2 So 4 Without Any Redox Speciesmentioning
“…When n = 1, the CPE can be considered as an ideal capacitor (Q = C d ) [29][30][31][32][33][34]. The "n" value of DDT SAM and IC-DDT SAM were 0.96 and 0.76, respectively.…”
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.