Desulfurization of CaO–Al2O3–SiO2–TiO2 Slag System

Abstract

The desulfurization ability of CaO-Al2O3-SiO2-TiO2 slag at 1 873 K was studied through the slag-metal desulfurization experiment by using a 10 kg inductive furnace and through theoretical calculation by using thermodynamic software FactSage. The experimental index considered were the sulfur distribution coefficient of the slag (LS) and the desulphurization ratio (ηS). The effect factors were binary basicity, the mass percentage of Al2O3 and TiO2. Research results are as follows. The effect of binary basicity is significant, compared with the mass percentage factors of Al2O3 and TiO2. Under the optimal experimental conditions, with the binary basicity is 7, the mass percentage of Al2O3 is 30% and TiO2 is 3%, the corresponding highest sulfur distribution coefficient for the slag are 58.14. While the content of TiO2 in the CaO-Al2O3-SiO2-TiO2 slag is in a range lower than 3-4%, the desulfurization ability of the CaO-Al2O3-SiO2-TiO2 slag is equal to that of the CaO-Al2O3-SiO2 slag. The slag system with TiO2 can meet the desulfurization requirements of steelmaking, which is a good way for resource utilization of solid waster containing titanium.

Effect of Al2O3, MgO, and CaO/SiO2on Viscosity of High Alumina Blast Furnace Slag

“…Chen et al optimized operating conditions for iron ore sintering with the orthogonal array tests. In addition, the orthogonal experimental design has been used to research desulfurization of CaO–Al 2 O 3 –SiO 2 –TiO 2 slag system, and the optimal combination of experimental condition with the best desulfurization ability of the slag can be derived . The optimized experimental design is found representatively, and all levels of each parameter have the same opportunities to appear in the experiments.…”

“…In addition, the orthogonal experimental design has been used to research desulfurization of CaO-Al 2 O 3 -SiO 2 -TiO 2 slag system, and the optimal combination of experimental condition with the best desulfurization ability of the slag can be derived. [6,7] The optimized experimental design is found representatively, and all levels of each parameter have the same opportunities to appear in the experiments. It can best guarantee to eliminate the interference between the various parameters.…”

Avaliação da substituição do CaF2 por B2 O3 em escórias sintéticas dessulfurantes no processo de refino secundário

“…Diante dos motivos citados, há uma tendência de diminuição do uso do CaF 2 na indústria siderúrgica e sua substituição por outros materiais menos nocivos ao meio ambiente. Diversos estudos têm sido conduzidos considerando a eliminação de CaF 2 [7,8] ou utilizando diferentes compostos (barrilha, sodalita, carbureto de cálcio, óxido de titânio, óxido de sódio) para este propósito [6][7][8][9][10][11][12]. Uma alternativa que tem se mostrado promissora é a utilização do óxido de boro, B 2 O 3 , como agente fluxante de escórias sintéticas.…”

Utilização De Óxido De Boro Como Fluxante De Escórias Sintéticas Dessulfurantes

“…Estes gases são agressivos ao meio ambiente, e até o momento não existe um substituto a nível industrial para ser aplicado. Diversos componentes foram testados em pesquisas [5][6][7][8][9], alguns deles são aplicados na composição das escórias (barrilha, sodalita, carbureto de cálcio, óxido de titânio). Um composto que vem sendo estudado é óxido de boro.…”