Design and Mechanical Characterization Using Digital Image Correlation of Soft Tissue-Mimicking Polymers

Abstract

Present and future anatomical models for biomedical applications will need bio-mimicking three-dimensional (3D)-printed tissues. These would enable, for example, the evaluation of the quality-performance of novel devices at an intermediate step between ex-vivo and in-vivo trials. Nowadays, PolyJet technology produces anatomical models with varying levels of realism and fidelity to replicate organic tissues. These include anatomical presets set with combinations of multiple materials, transitions, and colors that vary in hardness, flexibility, and density. This study aims to mechanically characterize multi-material specimens designed and fabricated to mimic various bio-inspired hierarchical structures targeted to mimic tendons and ligaments. A Stratasys® J750™ 3D Printer was used, combining the Agilus30™ material at different hardness levels in the bio-mimicking configurations. Then, the mechanical properties of these different options were tested to evaluate their behavior under uni-axial tensile tests. Digital Image Correlation (DIC) was used to accurately quantify the specimens’ large strains in a non-contact fashion. A difference in the mechanical properties according to pattern type, proposed hardness combinations, and matrix-to-fiber ratio were evidenced. The specimens V, J1, A1, and C were selected as the best for every type of pattern. Specimens V were chosen as the leading combination since they exhibited the best balance of mechanical properties with the higher values of Modulus of elasticity (2.21 ± 0.17 MPa), maximum strain (1.86 ± 0.05 mm/mm), and tensile strength at break (2.11 ± 0.13 MPa). The approach demonstrates the versatility of PolyJet technology that enables core materials to be tailored based on specific needs. These findings will allow the development of more accurate and realistic computational and 3D printed soft tissue anatomical solutions mimicking something much closer to real tissues.

Tensile and shear behavior of plain weave fabric carbon fiber reinforced polymer at elevated temperatures

“…The tests are carried out at a standard displacement rate as indicated by the ASTM standards because the viscoelastic response of the polymer‐based composites (including epoxy matrix systems) is more prominent when the strain rates are changed. [ 31,32 ] Besides, the goal of this study is to observe the differences in the tensile and in‐plane shear properties at different temperatures. The test setup inside the environmental chamber is presented in Figure 1.…”

Production of alginate macrocapsule device for long-term normoglycaemia in the treatment of type 1 diabetes mellitus with pancreatic cell sheet engineering

“…Also, early swelling prevents cellular proliferation and viability. However, the experiment was continued with 2% low alginate, which has a minimum swelling capacity, since excessive swelling will cause the material to degradation [52]. In this study, the water uptake ability of the macrocapsule is due to the difference in average porosity and pore size between the groups.…”

Exploring Machine Learning-Based Fault Monitoring for Polymer-Based Additive Manufacturing: Challenges and Opportunities

“…Due to its ability to recreate tangible objects using raw materials, its applications are endless. Its applications are not limited to industrial settings, as it is employed in areas including biomedical engineering, and civil engineering [ 7 , 8 ]. Additive manufacturing solutions are seen for orthopedic use in recreating body parts, creating machine parts, and even constructing houses.…”