Cyclic Polarization Study of Thick Welded Joints of Lean Duplex Stainless Steel for Application in Biodiesel Industry

Abstract

Thick welded joints of UNS S32304 lean duplex stainless steel (LDSS) has been studied in acidified glycerin, a byproduct of biodiesel plants, using cyclic polarization technique. LDSS S32304 thick plates were welded by different processes commonly employed in the fabrication process: shielded metal arc welding, gas metal arc welding and flux cored arc welding. The electrochemical behavior of different weldment zones was characterized. Transmission electron microscopy and scanning electron microscopy (SEM) were used for sample characterization. SEM images showed that the heat affected zone was the most critical zone for pitting corrosion for all samples. The results were associated to the microstructural features of the materials. Generally, the breakdown potential of the top regions of welds was higher in acidified glycerin than the weld root for welds fabricated with two different filler metals. Basically, all the welded samples exhibited similar or higher corrosion resistance, compared with the corresponding base metal.

Efeito Da Temperatura De Recozimento Na Corrosão Por Pite Do Aço Inoxidável Lean Duplex Uns S32304

“…Observaram-se regiões passivas largas para todas as amostras e potenciais de pites bastante superiores ao correspondente potencial de circuito aberto. Estas observações indicam que as amostras apresentaram excelente resistência ao início da corrosão por pite nesse ambiente de cloretos [6]. Considerando o desvio padrão, não foram observadas diferenças significativas nos valores de OCP.…”

“…A polarização mostrou uma histerese positiva, de modo que as amostras não apresentaram capacidade de repassivação em meio contendo cloreto. Isso indica que a corrosão por pite quando iniciada, mesmo em valores de potenciais próximos ao potencial de circuito aberto, pode ocorrer por longos períodos [6]. Avaliando a resistência à corrosão, observou-se que a amostra laminada a quente apresentou potencial de pite similar àquela recozida a 1100°C durante 1800s.…”

“…Os aços inoxidáveis duplex (AID) estão sendo amplamente utilizados como alternativas para aços inoxidáveis austeníticos e ligas à base de níquel [5]. Representam uma classe importante de aços com uma combinação de resistência mecânica e à corrosão em ambientes contendo íons cloreto [6]. A fim de proporcionar a melhor combinação de resistência à corrosão e resistência mecânica do AID, a microestrutura deve ser constituída por quantidades aproximadamente iguais de fases austeníticas e ferríticas, bem como a falta de precipitação de fases secundárias prejudiciais tais como σ, χ, Cr 23 C 6 e Cr 2 N [7,8].…”

Effect of Warm Rolling on the Corrosion and Mechanical Properties of UNS S32205 Duplex Stainless Steel

“…The number of applications for DSS increases and new alloys are continuously developed due to the volatility of the Ni price. The nickel content can be partially replaced by manganese and nitrogen in these alloys 3,4 . The microstructure comprised of approximately equal amounts of austenite (γ) and ferrite (α) phases and the lack of secondary phases such as σ, M 23 C 6 and Cr 2 N provides the advantage of mechanical properties along with corrosion resistance as compared to the usual single-phase stainless steels 5,6,7 .…”

Resistência À Corrosão Do Filme Passivo Formado No Aço Inoxidável Duplex 2205 Laminado a Morno

“…Os aços inoxidáveis duplex (AID) estão sendo amplamente utilizados como alternativas para aços inoxidáveis austeníticos e ligas à base de níquel [1]. Rrepresentam uma classe importante de aços com uma combinação de resistência mecânica e à corrosão em ambientes contendo íons cloreto [2]. Os AID apresentam uma microestrutura formada por quantidades aproximadamente iguais de austenita (ɣ) e ferrita (α) e suas melhores propriedades permitem que sejam muito utilizados na indústria química, petroquímica, marítima, nuclear e de papel [3,4].…”