Crevice corrosion behavior of A516-70 carbon steel in solutions containing inhibitors and chloride ions

Materials selection for thermal energy storage systems in parabolic trough collector solar facilities using high chloride content nitrate salts

“…Then, lack of knowledge has been detected about long term corrosion tests with nitrates salts containing chloride percentages higher than 1% by weight which would analyze the effect of low purity salts over metallic materials used in CSP facilities. Moreover, although the negative impact of chlorides over corrosion phenomena such as crevice corrosion and stress corrosion cracking (SCC) has been reported for different corrosive fluids [25][26][27][28], results associated to high chloride content nitrate salts have not been identified in the state of the art.…”

Quantitative analysis of localized corrosion in tensile armor wire of flexible riser submitted to sweet stress corrosion cracking testing with crevice

“…Yang et al [22] compared current density and fluctuations of inverse potential corrosion when the pitting corrosion phase of A516 steel (0.35% C) in the chloride ion solution is reached. During the time of immersion, fluctuations became more frequent.…”

Corrosion propagation monitoring using electrochemical noise measurements on carbon steel in hydrogenocarbonated solution containing chloride ions

“…Localized corrosion of carbon steel induced by chloride ions in these environments was also studied by Electrochemical Noise Measurements (ENM) to detect the onset of corrosion, identify its mechanism and quantify the damage caused by a given corrosion mode [6,[12][13][14]. It is well known that ENM presents potentialities for such application [15,16].…”