Corrosion behavior of Monofrax K‐3 refractory in borosilicate‐based model low activity waste glass melts

Abstract

Owing to its good chemical and thermal durabilities at high temperatures, Monofrax K-3 refractory is widely used in nuclear waste vitrification as a lining material in melting vessels. However, the corrosion of K-3 refractory during the vitrification of nuclear waste is a serious problem because it affects the melter's safety, performance, and lifetime. Therefore, in the present study, we have focused on unearthing the impact of glass network formers, such as SiO 2 , B 2 O 3 , and Al 2 O 3 , in a model nuclear waste glass composition on the corrosion of Monofrax K-3 refractory. The corrosion tests have been performed per ASTM C621 at 1150 • C for 5 days. The dimensional measurements on corroded K-3 refractory suggest that Al 2 O 3 and SiO 2 tend to reduce the refractory corrosion (neck loss), with the effect of Al 2 O 3 being significant. A corroded region on the K-3 refractory at the melt-refractory interface is observed. The corrosion occurs via a coupling of the melt infiltration induced by a capillary effect and the dissolution of Al, Mg, and Fe components from K-3 into the melt through chemical reactions. A Cr-rich layer is retained on the glass contact surface of the corroded K-3 refractory.