Conductance investigation of p-MIECs fabricated by poly(3,4-ethylenedioxy thiophene), polyacrylic acid, polyethylene oxide, and lithium-ion salt

Abstract

Polymer blends and composite films were facilely prepared from their aqueous solutions with varying contents of poly(3,4-ethylenedioxythiophene) (PEDOT), polyethylene oxide (PEO), and polyacrylic acid (PAA). The physicochemical and electric properties of the composite films were analyzed by Raman spectra, infrared spectra (FT-IR), scanning electronic microscopy (SEM), thermogravimetric analysis (TGA), and four-point probe method. PEDOT was successfully incorporated into each blend which was confirmed by spectra analysis. The crystallization of PAA or PEO and the structure of PEDOT should be taken into consideration for the electronic conductivity. According to Raman spectra, in the case of PEDOT-PAA-PEO, conformation of the PEDOT backbone changed from the quinoid to the benzoid structure partly. The ionic conductivities of lithium-ion salt-mixed PAA-PEO and ternary blend were characterized by AC impedance spectroscopy. The ternary blend with LiCoO 2 presents good electronic and ionic conductivity, and it appears to be a new candidate for polymeric mixed ionic electronic conductor. POLYM. COMPOS., 36:2076-2083, 2015

Preparation and Swelling Properties of Poly(3,4–Thylenedioxythiophene)/Poly(Acrylic Acid)/bentonite Composite Hydrogels

“…A broad peak at about 1000 cm -1 and peaks at about 790 cm -1 prominently observed in BNT disappeared in the PAA/BNT composite. The peaks at 1400 and 1550 cm -1 in the PAA/BNT composite can correspond to the out-of-plane C-O-H binding of PAA and the CH2 group asymmetric stretching of PAA, respectively [20,21]. The characteristic bands of PEDOT are the asymmetric stretching of the C=C bond at about 1490 cm -1 , the intertwining stretching of the C-C bond at about 1304 cm -1 , the C-O-C bending vibrational band in the ethylenedioxy group at around 1040, 1163 and 1280 cm -1 [22].…”