Compressive and flexural behavior of glass fiber-reinforced concrete

Abstract

Utilizing fibre-reinforced concrete is still a difficulty for present engineers. Generally, it is acknowledged that the mechanical, cracking and fracture qualities of fibre-reinforced concrete are much better than those of conventional concrete. The addition of fibres to the concrete matrix mitigates its fragility. Typically, short fibres are utilised in concrete to prevent cracks caused by drying and autogenous shrinkage. Currently, there is a substantial increase in the use of short alkali-resistant glass fibres. This experiment was conducted to examine the influence of glass fibre reinforcement on the compressive and flexural behaviour of concrete. This research investigates the characteristics of glass fibres reinforced concrete (GFRC) after 7 and 28 days of curing, such that GFRC may be employed in construction. Concrete containing short alkali-resistant glass fibres of 36 mm in length and 1% volume fraction (VF) was developed for this purpose. The testing findings revealed that the average compressive strength of GFRC after 28 days of curing was 72.06 MPa. The flexural properties of GFRC are determined, and the 7-day and 28-day average bending strengths of GFRC concrete samples are 6.46 MPa and 7.94 MPa, respectively, indicating that GFRC responds well under loading conditions.

Fin Sandy Concrete Reinforced with Macro Polypropylene Fiber for Rural And Desert Housing

“…Meanwhile apart from the use of steel fibers, a third trend has appeared where the engineer chooses to use fibers produced industrially, such as glass fiber (Annamaneni 2023)., polyester fiber (Mohsin 2020), carbon fiber (Ghanem 2019), macro synthetic fibers (Bolat 2014), and polypropylene fibers Ravishankar (2021).…”