This study focuses on developing an alternative membrane for PEMFC due to the disadvantages of using Nafion. Fluoroboric acid (FBA) was used as an additive material to SPEEK-PVA blend membranes at different weight ratios (1%, 5%, 7.5%, 10%, and 12.5%), and a synthesis procedure was carried out with the solution-casting. Thermal crosslinking was performed with all membranes. Utilizing FBA, with its highly electronegative fluorine groups, is a novel approach expected to enhance proton conductivity. The structural, morphological, and thermal properties of the synthesized membranes were determined by FTIR, XRD, SEM, TGA-DTG, and DSC. Water uptake capacity (WUC), swelling property, area change, dynamic mechanical analysis, ion exchange capacity (IEC), AC impedance analysis, hydrolytic stability, and oxidative stability analyses were performed for fuel cell applications. Although FBA does not have a crystal structure, the synergy it created with the SPEEK-PVA membrane increased the crystallinity of the membrane and, accordingly, glass transition temperature. SEM images of membranes at a ratio above 7.5% show that agglomerations occur in the structure and this is supported by other analyses. It was determined that the membrane composition with the highest WUC (16.44%), IEC (1.55 meq/g), and proton conductivity (0.57 S/cm) values contained 7.5% FBA from the characterization studies, and a single-cell performance test was actualized with this. 418 mA/cm2 current density and 250.8 mW/cm2 power density were obtained at 0.6 V cell potential, with the membrane containing 7.5% FBA. This study shows that the synthesized membrane, especially the FBA, is a promising option for PEMFC application. Graphical Abstract
This study focuses on developing an alternative membrane for PEMFC due to the disadvantages of using Nafion. Fluoroboric acid (FBA) was used as an additive material to SPEEK-PVA blend membranes at different weight ratios (1%, 5%, 7.5%, 10%, and 12.5%), and a synthesis procedure was carried out with the solution-casting. Thermal crosslinking was performed with all membranes. Utilizing FBA, with its highly electronegative fluorine groups, is a novel approach expected to enhance proton conductivity. The structural, morphological, and thermal properties of the synthesized membranes were determined by FTIR, XRD, SEM, TGA-DTG, and DSC. Water uptake capacity (WUC), swelling property, area change, dynamic mechanical analysis, ion exchange capacity (IEC), AC impedance analysis, hydrolytic stability, and oxidative stability analyses were performed for fuel cell applications. Although FBA does not have a crystal structure, the synergy it created with the SPEEK-PVA membrane increased the crystallinity of the membrane and, accordingly, glass transition temperature. SEM images of membranes at a ratio above 7.5% show that agglomerations occur in the structure and this is supported by other analyses. It was determined that the membrane composition with the highest WUC (16.44%), IEC (1.55 meq/g), and proton conductivity (0.57 S/cm) values contained 7.5% FBA from the characterization studies, and a single-cell performance test was actualized with this. 418 mA/cm2 current density and 250.8 mW/cm2 power density were obtained at 0.6 V cell potential, with the membrane containing 7.5% FBA. This study shows that the synthesized membrane, especially the FBA, is a promising option for PEMFC application. Graphical Abstract
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.