Comparative study on interaction between rare earth oxide refractories and rare earth treated steel

Meng, Ze; Li, Guang-qiang; Yuan, Cheng; Zhao, Yi-jiang; Zheng, Qing; Zeng, Bin; Liu, Yu

doi:10.1007/s42243-023-01123-z

Cited by 2 publications

(1 citation statement)

References 34 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…In contrast, an interface layer of MgO•Al 2 O 3 and a transition layer of CaO-Al 2 O 3 were observed at the interface between MgO-C refractory and high Mn-high Al steel in the study of Wang et al [24] In the cases of other types of refractories, many studies were also carried out. For instance, Deng et al [18] pointed out that the reaction of Al 2 O 3 refractory with Si-Mn-killed steel could increase the melting point of SiO 2 -Al 2 O 3 -MnO and SiO 2 -Al 2 O 3 -CaO inclusions in steel, while Meng et al [25] observed a dense Ce 2 O 2 S layer formed at interface between CeAlO 3 refractory and a rare earth-treated steel, which further hindered the interaction between the refractory and the steel.…”

Section: Introductionmentioning

confidence: 99%

Study on High‐Temperature Reactions of MgO Refractory with Ti‐Bearing Al‐Killed Steel

Yang,

Deng,

Zhu

2024

steel research int.

View full text Add to dashboard Cite

To understand the interaction behaviors between MgO refractory and Ti‐bearing Al‐killed steel grades, laboratory experiments are conducted at different times using different steel grades containing different Ti contents (w[Ti] = 0–0.2%). The results show that when MgO refractory reacts with Ti‐free Al‐killed steel, an MgO–Al2O3 spinel‐reacted layer can be detected at the steel‐refractory boundary. In the case of Ti‐bearing Al‐killed steel, an MgO–Al2O3–TiOx system‐reacted layer is formed at the edge of MgO refractory, and the thickness of the layer and the TiOx content in the layer increase with the increase of reaction time and the dissolved Ti content in steel. Thermodynamic calculations indicate that the MgO–Al2O3–TiOx system layer is a spinel solid solution, and is the stable phase in Ti‐bearing Al‐killed steel. In addition, the melting point of the reacted layer declines with the increase of TiOx. Therefore, the corrosion of MgO refractory by Ti‐bearing steel grades is more serious than that by conventional steel grades, and it also leads to the formation of MgO–Al2O3–TiOx system macroinclusions in steel.

show abstract

Section: Introductionmentioning

confidence: 99%