Combination of TEM and 3D atom probe study of microstructure and alloy carbide in a Nb-V micro-alloyed steel tempered at 650 °C

Liu, Qing-Dong; Liu, Wenqing; Zhao, Shuyu

doi:10.1007/s12540-013-4018-2

Cited by 3 publications

(1 citation statement)

References 14 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…The C content of the carbon-rich layer is much higher than that of the 45 steel substrate. This is because Zn and Al are non-carbide forming elements, which cause the C atom crowding-out effect during the formation of the diffusion layer [34]. Therefore, the diffusion layer will have a carbon-rich layer near the substrate.…”

Section: Resultsmentioning

confidence: 99%

Microstructure and Corrosion Resistance of Zn-Al Diffusion Layer on 45 Steel Aided by Mechanical Energy

Tong

Liang²,

Wei³

et al. 2019

Materials

View full text Add to dashboard Cite

In harsh environments, the corrosion damage of steel structures and equipment is a serious threat to the operational safety of service. In this paper, a Zn-Al diffusion layer was fabricated on 45 steel by the Mechanical Energy Aided Diffusion Method (MEADM) at 450 °C. The microstructure and composition, the surface topography, and the electrochemical performance of the Zn-Al diffusion layer were analyzed before and after corrosion. The results show that the Zn-Al diffusion layer are composed of Al2O3 and Γ1 phase (Fe11Zn40) and δ1 phase (FeZn6.67, FeZn8.87, and FeZn10.98) Zn-Fe alloy. There is a transition zone with the thickness of about 5 μm at the interface between the Zn-Al diffusion layer and the substrate, and a carbon-rich layer exists in this zone. The full immersion test and electrochemical test show that the compact corrosion products produced by the initial corrosion of the Zn-Al diffusion layer will firmly bond to the Zn-Al diffusion layer surface and fill the crack, which plays a role in preventing corrosion of the corrosive medium and reducing the corrosion rate of the Zn-Al diffusion layer. The salt spray test reveals that the initial corrosion products of the Zn-Al diffusion layer are mainly ZnO and Zn5(OH)8Cl2H2O. New corrosion products such as ZnAl2O4, FeOCl appear at the middle corrosion stage. The corrosion product ZnAl2O4 disappears, and the corrosion products Zn(OH)2 and Al(OH)3 appear at the later corrosion stage.

show abstract

Section: Resultsmentioning

confidence: 99%