Chromophore Poling in Thin Films of Organic Glasses. 3. Setup for Corona Triode Discharge / Hromoforu Polarizēšana Plānās Organisko Stiklu Kārtiņās 3. Koronas Izlādes Triodes Ierīce

Abstract

The corona discharge is described focusing on the advantages of corona triode techniques for the direct current (DC) positive poling of optical polymers. The proposed experimental setup allows the corona poling of nonlinear optical (NLO) polymers in the modes of DC constant current (the lowest 1nA) and of the fixed corona-grid voltage, making it possible to carry out the corona-onset poling at elevated temperature (COPET) up to 200 oC. The setup also provides a wide range of the corona discharge voltage (3 kV - 15 kV), variable reciprocal distance of electrodes as well as the possibility to choose from different types of the corona electrode (needle, multi-needle, wire, etc.). By keeping the corona-to-grid voltage constant, a stable corona discharge at electrode is attained. The grid voltage can be varied in the range from 0 to 3kV. The corona poling area on the sample surface is pre-defined by placing ring spacers above it. The setup is completely computerized, allowing both control and monitoring of the corona discharge, which promotes research into the process of charging NLO polymer samples and selection of the optimal poling mode. Using the voltage-current characteristics and the second-harmonic measurements of a poled polymer we also demonstrate the influence of the setup parameters on the efficiency of poling the thin film NLO polymers.

Review and comparison of experimental techniques used for determination of thin film electro-optic coefficients

“…Typical thickness of the polymer thin films varied from 1.5 to 2.2 μm, but the refractive index was 1.54 at 632 nm and the absorption maximum was at 490 nm. To obtain a non‐centrosymmetric order in the polymer films the samples were poled using a computer controlled corona triode device . The m‐line method was used to confirm that the material had not obtained a significant birefringence during the poling suggesting only a weak poling of the films.…”