ChemInform Abstract: FACTORS INFLUENCING THE LIFETIME OF PURE BETA‐ALUMINA ELECTROLYTE

Lazennec, Y.; Lasne, C; Margotin, P.; Fally, J.

doi:10.1002/chin.197535028

Chemischer Informationsdienst

1975

DOI: 10.1002/chin.197535028

|View full text |Cite

ChemInform Abstract: FACTORS INFLUENCING THE LIFETIME OF PURE BETA‐ALUMINA ELECTROLYTE

Y. Lazennec¹,

C Lasne²,

P. Margotin³

et al.

Abstract: Der Einfluß einiger Verunreinigungen auf das Alter und die Lebensdauer von Na‐S‐ und Na‐Na‐Batterien mit β‐Al2O3 als Elektrolyt wird untersucht.

Help me understand this report

Search citation statements

Order By: Relevance

Paper Sections

Select...

Citation Types

Supporting

Mentioning

Contrasting

Year Published

1978

Publication Types

Select...

Article1

Relationship

Self Cite0

Independent1

Authors

Journals

Cited by 1 publication

(1 citation statement)

References 1 publication

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Impurities can degrade the performance and life of the ~"-alumina electrolyte in a sodium-sulfur cell (1)(2)(3)(4)(5)(6). In the absence of an electric field potassium exchanges with sodium in large grains in ~-alumina in contact with a sodium source, and cracks result (6).…”

mentioning

confidence: 99%

Effects of Calcium, Potassium, and Iron Ions on Degradation of β″‐Alumina

Yasui

Doremus

1978

J. Electrochem. Soc.

View full text Add to dashboard Cite

The influence of calcium, potassium, and iron impurities in sodium-sulfur cells on ~"-alumina electrolytes were studied. Sections of the ceramic were analyzed with the electron microprobe after cyclic electrolysis of the cells. No degradation by iron was detected. The distribution of potassium in the ~"-alumina became more uniform as electrolysis proceeded, and the cell impedance increased by factors of two or three. Calcium was the most damaging impurity; even in small concentrations it caused large increases in cell impedance and calcium concentrated in the grain boundaries of the ~"-alumina.Impurities can degrade the performance and life of the ~"-alumina electrolyte in a sodium-sulfur cell (1-6). In the absence of an electric field potassium exchanges with sodium in large grains in ~-alumina in contact with a sodium source, and cracks result (6). In this work the influence of potassium, calcium, and iron impurities on degradation of ~-alumina after cyclic electrolysis was studied with the electron microprobe and the scanning electron microscope. Calcium was found to be the most damaging impurity; even in small concentrations it causes large increases in the resistance of p"-alumina, and can also cause it to crack.Experimental Two different cells were used, as shown in Fig. I. In one there was sodium inside the ~"-alumina tube and sulfur-polysulfide outside; in the other there was Na2S4 in both chambers. Impurities were added to the outer chamber as sulfides.Two different ~"-aluminas were used, one with 9.0% Na20 and 0.8% Li20 (9.0-0.8) and the other with 8.85% Na~O and 0.75% Li20 (8.85-0.75).The cells were baked at 850~ for 12 hr at 0.02 mm Hg before filling. Sulfur (sublimed) was dried under a reduced pressure at about 70~176 and sodium was filtered through a glass frit at about 150~ Commercial Na2S4 (Alfa) was washed with toluene and then dried in vacuum at 130~ for 48 hr. All reactants were placed into the cell under a dry atmosphere and then melted into the cell. The cell was sealed with dry argon at a third of atmospheric pressure. For the Na/S cells 15g of Na and 30g of S were used.The Na/S cells were first discharged until the composition of the outer chamber reached about Na2S4, and then charged and discharged in a 4 hr cycle. The current density was 25-30 mA/cm 2 for both charging and discharging, and this value was low enough to exclude the possibility of degradation due to the high current density mechanism. The composition of the outer chamber was near Na2S4, owing to the short " Electrochemical Society Active Member.cycle time and the low current density. Simulation cells were also operated in 4 hr cycles with a current density of 25-30 mA/cm 2. wir "ex 32 dun lit ~lun,. ,a ~11 elt Fig. I. Structures of Na-S cells and simulation cells 1a2S4 100'/ ) unless CC License in place (see abstract). ecsdl.org/site/terms_use address. Redistribution subject to ECS terms of use (see 169.233.248.124 Downloaded on 2015-03-31 to IP

show abstract

mentioning

confidence: 99%

Effects of Calcium, Potassium, and Iron Ions on Degradation of β″‐Alumina

Yasui

Doremus

1978

J. Electrochem. Soc.

View full text Add to dashboard Cite

show abstract

scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.

Contact Info

customersupport@researchsolutions.com

10624 S. Eastern Ave., Ste. A-614

Henderson, NV 89052, USA

Blog Terms and Conditions API Terms Privacy Policy Contact Cookie Preferences Do Not Sell or Share My Personal Information

Made with 💙 for researchers

Part of the Research Solutions Family.

ChemInform Abstract: FACTORS INFLUENCING THE LIFETIME OF PURE BETA‐ALUMINA ELECTROLYTE

Abstract: Der Einfluß einiger Verunreinigungen auf das Alter und die Lebensdauer von Na‐S‐ und Na‐Na‐Batterien mit β‐Al2O3 als Elektrolyt wird untersucht.

Cited by 1 publication

References 1 publication

Effects of Calcium, Potassium, and Iron Ions on Degradation of β″‐Alumina

Effects of Calcium, Potassium, and Iron Ions on Degradation of β″‐Alumina