Characteristics of fresh mortar with particle size and replacement ratio of copper slag

Abstract

It is estimated that over 2 million tons of non-ferrous wastes are generated after refining. Up to now, most researches were focused on extracting precious metals and there were very few research on the utilization of the slag byproduct. In this study, we studied to evaluate whether copper slag could be used as aggregates in concrete. Fresh mortar were evaluated on the particle size and replacement ratio of the copper slag with river-sand. Experimental results indicated that flow, air content and drying shrinkage of concrete varied with particle size, which confirmed that proper classification of copper slag is very important. And, setting time and unit weight of the concrete increased with replacement ratio. When particle size of the slag was similar to the river-sand, concrete with copper slag showed slump, air content, setting time, drying shrinkage and unit weight became larger compared to the concrete using river-sand only. Therefore, it is believed that proper classification and replacement ratio should be optimized for the effective use of slag in concrete.

Strength and sulfuric acid resistance properties of cement mortar containing copper slag

“…산업부산물의 일종인 고로슬래그, 플라이애쉬 등은 콘크리트 혼화재로서 사용하기 위해 그동안 활발한 연구 개발이 진행되었고, 활용도도 증가되어 있는 실정이다 [2]. 또한 동 제련 과정에서 발생되는 동 슬래그는 국내에 서 년간 70만톤 이상이 발생되고 있으며 건설용 소재로 서 활용하기 위한 연구가 진행되고 있다 [2][3][4][5].…”

“…산업부산물의 일종인 고로슬래그, 플라이애쉬 등은 콘크리트 혼화재로서 사용하기 위해 그동안 활발한 연구 개발이 진행되었고, 활용도도 증가되어 있는 실정이다 [2]. 또한 동 제련 과정에서 발생되는 동 슬래그는 국내에 서 년간 70만톤 이상이 발생되고 있으며 건설용 소재로 서 활용하기 위한 연구가 진행되고 있다 [2][3][4][5]. 국내의 동 제련 슬래그의 활용에 관한 연구는 시멘트 및 콘크리트용 골재 뿐만 아니라, 철도 노반재료, 샌드블 라스팅재, 지반개량재, 케이슨 채움재료 등으로 활용하기 위한 연구가 진행되고 있다 [5][6][7][8] Table 1 The composition of the CS-A, CS-B and CS-C samples and experimental design …”