Carbon Fiber Reinforced Multi-Phase Epoxy Syntactic Foam (CFR-Epoxy-Hardener/HGMS/Aerogel-R-Hollow Epoxy Macrosphere(AR-HEMS))

Reducing the structural load and operational energy consumption of buildings is a trend in the development of the construction industry, and lightweight concrete has become a research hotspot because of its dual characteristics of low density and high strength. In this paper, a three-step method is used to prepare lightweight concrete composites. In the first step, basalt fiber powder was adhered to polystyrene foam ball expanded polystyrene spheres (EPSs) by the “ball rolling method” to obtain basalt fiber reinforced epoxy composite balls. In the second step, the epoxy resin composite ball and the configured cement matrix are filled into a prefabricated mold. Finally, the lightweight concrete specimens were overlaid, pressed into shape, and cured for 28 days. By changing the volume ratio, size, and wall thickness of the epoxy composite balls, as well as the length and content of basalt fibers, the lightweight concrete was exhibited a reduction in density and increase in strength. The results showed that the smaller the epoxy composite spheres and the larger the wall thickness are, the higher the compressive strength of the material for a certain volume ratio of epoxy composite spheres will be. The addition of appropriate hollow glass beads can reduce the number of pores in the matrix, but excessive hollow glass beads will reduce the bonding force of the concrete matrix. Basalt fibers not only improve the strength of EPSs but also serve to connect matrix–matrix and matrix–epoxy composite spheres.

show abstract

Study of the Compressive Properties of Heavy Calcium Carbonate-Reinforced Epoxy Composite Spheres (HC-R-EMS) Composite Lightweight Concrete

Chen

Jiang

et al. 2023

Polymers

View full text Add to dashboard Cite

Lightweight concrete is one of the effective means to solve the problems of structural component weight, energy efficiency, and fire safety in modern civil engineering. Heavy calcium carbonate-reinforced epoxy composite spheres (HC-R-EMS) were prepared by the ball milling method, and HC-R-EMS, cement, and hollow glass microspheres (HGMS) were mixed into the mold by the molding method to prepare composite lightweight concrete. The relationship between the HC-R-EMS volumetric fraction, the initial inner diameter of the HC-R-EMS, the number of layers of HC-R-EMS, the HGMS volume ratio, the basalt fiber length and content, and the multi-phase composite lightweight concrete density and compressive strength was studied. The experimental results show that the density of the lightweight concrete ranges between 0.953–1.679 g/cm3 and the compressive strength ranges between 1.59–17.26 MPa, where the volume fraction of HC-R-EMS is 90%, the initial internal diameter is 8–9 mm, and the number of layers of HC-R-EMS is three. The lightweight concrete can meet the requirements of high strength (12.67 MPa) and low density (0.953 g/cm3). In addition, the addition of basalt fiber (BF) can effectively improve the compressive strength of the material without changing the density of the material. From a micro-level perspective, HC-R-EMS is closely combined with the cement matrix, which is conducive to increasing the compressive strength of concrete. Basalt fibers connect the matrix into a network, improving the maximum limit force of the concrete.

show abstract

scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.

Contact Info

hi@scite.ai

10624 S. Eastern Ave., Ste. A-614

Henderson, NV 89052, USA

Blog Terms and Conditions API Terms Privacy Policy Contact Cookie Preferences Do Not Sell or Share My Personal Information

Made with 💙 for researchers

Part of the Research Solutions Family.

Carbon Fiber Reinforced Multi-Phase Epoxy Syntactic Foam (CFR-Epoxy-Hardener/HGMS/Aerogel-R-Hollow Epoxy Macrosphere(AR-HEMS))

Cited by 4 publications

References 24 publications

Synthesis and characterization of EPS reinforced modified castor oil-based epoxy biocomposite

Synthesis and characterization of EPS reinforced modified castor oil-based epoxy biocomposite

Experimental study on the effect of basalt fiber reinforced expanded polystyrene foams on the compressive strength of lightweight concrete

Study of the Compressive Properties of Heavy Calcium Carbonate-Reinforced Epoxy Composite Spheres (HC-R-EMS) Composite Lightweight Concrete

Contact Info

Product

Resources

About