Calcium hydroxide attack on rocks

Way, Steve; Cole, W. F.

doi:10.1016/0008-8846(82)90022-9

Cited by 12 publications

(5 citation statements)

References 4 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Initially, this phenomenon was examined with regards to possible formation of expansive gel, which may distress the material similarly to ASR, however, in plentiful calcium hydroxide conditions, no such behavior was observed (Way and Cole 1982). Nonetheless, as a consequence of alkali oxides leaching into the pore solution, the increased alkali content may lead to destabilization of other silicates in the aggregate.…”

Section: Reaction Of Hardened Cement Paste and Feldspar Mineralsmentioning

confidence: 99%

Long-term Material Properties of a Thick Concrete Wall Exposed to Ordinary Environmental Conditions in a Nuclear Reactor Building: the Contribution of Cement Hydrates and Feldspar Interaction

Rymeš

Maruyama

Shimamoto

et al. 2019

ACT

View full text Add to dashboard Cite

A variation of material properties with depth is observed in a massive, seismic-resistant internal wall of Unit 1 of the Hamaoka Nuclear Power Plant (NPP) 45 years after its construction. The maximum values are attained in the center of the structural element and gradually decrease towards the surface, while still well exceeding the required performance. It is found that this trend can be mostly attributed to the reaction between cement hydrates and rock-forming minerals of a feldspar group, which releases silica and alumina oxides into the pore solution, where they react with portlandite to form new hydrates. No evidence of expansive distress similar to the alkali-silica reaction (ASR) is found in the material, owing to this reaction. Possible implications for the aging management of existing concrete structures are discussed. 1

show abstract

Section: Reaction Of Hardened Cement Paste and Feldspar Mineralsmentioning

confidence: 99%

Long-term Material Properties of a Thick Concrete Wall Exposed to Ordinary Environmental Conditions in a Nuclear Reactor Building: the Contribution of Cement Hydrates and Feldspar Interaction

Rymeš

Maruyama

Shimamoto

et al. 2019

ACT

View full text Add to dashboard Cite

show abstract

“…Así, podemos apreciar si los áridos son o no reactivos dependiendo de los efectos que la reacción árido-álcali ha causado en cada superficie en un punto determinado (19)(20)(21)(22). Por ejemplo, en el estudio de una de las corneanas se aprecia como se disuelve el cristal de biotita después del tratamiento alcalino (Figura 6).…”

Section: Método De Reactividad Superficial: Microscopía Electrónica Dunclassified

“…The results obtained upon studying the surfaces of the aggregates allowed us to determine whether an alkali-aggregate reaction had taken place (19)(20)(21)(22). For example, it was clear upon studying one of the hornfels that the biotite crystals had dissolved upon base treatment ( Figure 6).…”

Section: Surface Reactivity Investigation: Scanning Electron Microscomentioning

confidence: 99%

Reactividad árido-álcali en áridos empleados para hormigón

et al. 2010

View full text Add to dashboard Cite

RESUMENEste trabajo pretende contribuir al conocimiento de las reacciones de interacción entre los áridos y los componentes de la fase intersticial del hormigón y determinar si estos áridos, empleados posteriormente en la fabricación del hormigón, son reactivos y por tanto susceptibles de provocar una disminución progresiva de sus propiedades iniciales.Para la caracterización de cada árido se ha realizado un estudio petrográfico, fundamental a la hora de determinar su posterior comportamiento en términos de reactividad frente a diversos factores. Seguidamente, se ha analizado la reactividad potencial de diferentes áridos silicatados (pizarras, gneis, corneanas, granitos, cuarcita y serpentina) mediante los dos métodos normalizados existentes: el método químico para la determinación de la reactividad potencial de áridos y el método acelerado en probetas de mortero; y para contrastar ambos hemos seguido el método de la reactividad superficial.Los resultados determinan que algunos áridos son susceptibles de reaccionar con los componentes de la fase intersticial de hormigón. La observación de su textura antes y después del ataque denota la existencia de esta interacción.Palabras clave: reacción álcali-sílice, degradación, expansión, mortero, SEM. SUMMARYThe aim of this work is to contribute to the knowledge of the interactions between aggregates and the components of the interstitial phase of concrete and to determine whether those aggregates that are subsequently used in the manufacture of concrete are reagents and are therefore likely to undergo a progressive deterioration of their initial properties.An initial petrographic study of each aggregate is performed in order to be able to determine its subsequent behaviour and reactivity under the influence of various factors. The potential reactivity of different silicaceous aggregates (slates, gneiss, hornfels, granites, quartzite and serpentine) is then determined by a chemical method for evaluating the potential reactivity of aggregates and an accelerated method in mortar specimens, and finally the surface reactivity is investigated.The results of these studies suggest that some aggregates are able to react with the components of the interstitial phase of concrete. The existence of this kind of interaction is confirmed by the results of the surface investigations before and after the basic reaction.Keywords: alkali-silica reaction, degradation, expansion, mortar, SEM. INTRODUCCIÓNUna reacción álcali-silicato se produce cuando interaccionan áridos, que contienen minerales silicatados potencialmente reactivos, con los álcalis del cemento. Esta reactividad lleva consigo la formación de geles que en presencia de humedad se expanden, manifestándose en agrietamientos y movimientos diferenciales y con ello, una disminución drástica de la durabilidad (1-5) Por tanto, este proceso viene determinado en gran medida con la humedad relativa del ambiente y la tensión mecánica a la cual esta sometida cada elemento estructural (6-11).Las fases de la reacción árido-álcali se pueden...

show abstract

“…5 g de esta fracción se trataron con 40 ml de disolución saturada de hidróxido cálcico o con disolución 1N de hidróxido sódico. Este procedimiento es similar al utilizado por Way and Cole (1982) con pequeñas diferencias; así, la temperatura de reacción se mantuvo a 25°C en lugar de los 50°C y el tiempo de reacción en 28 días en lugar de 40 días. Transcurrido ese tiempo se filtraron las disoluciones y se determinaron las concentraciones de Si, Al, Ca, P, Na y K en un espectrómetro ICP-OES Perkin Elmer 4300DV.…”

Section: Muestras Estudiadas Y Métodos Experimentalesunclassified

Reactividad potencial de las rocas andesíticas de Cabo de Gata (SE de España)

Soriano

Iglesia²,

García-Calleja

et al. 2010

Estud. geol.

View full text Add to dashboard Cite

IntroducciónLa durabilidad de un material se puede definir como la capacidad de mantener un adecuado comportamiento, propiedades y condiciones de seguridad, durante el tiempo y las condiciones de servicio previstas para su empleo. En el caso del hormigón, la durabilidad es la capacidad para resistir ataques físicos, fisicoquímicos y químicos tanto de origen interno como externo (ACI Committee 201, 2007).Cuando hay que evaluar la influencia ejercida por diversos factores en la durabilidad del hormigón nos encontramos con el grave problema de la importancia relativa que los diferentes autores prestan a cada uno de los factores indicados. Así, los de formación más técnica tiende a conceder mayor importancia a los aspectos mecánicos y físicos que a los químicos y fisicoquímicos. Por el contrario, los de formación más científica tienden a considerar principalmente los factores de tipo químico o fisicoquímico tales como composición del cemento, reactividad de los áridos, etc.Algunos áridos de naturaleza silícea pueden tener una elevada reactividad potencial, ya que reaccionan con los álcalis de la fase intersticial del hormigón, dando lugar a la formación de geles y compuestos de sílice. En general, estos compuestos tienen capacidad para generar en presencia de agua una elevada presión osmótica, lo que da lugar a un aumento de volumen y a importantes presiones disruptivas. Reactividad potencial de las rocas andesíticas de Cabo de Gata (SE de España)

show abstract

Calcium hydroxide attack on rocks

Cited by 12 publications

References 4 publications

Long-term Material Properties of a Thick Concrete Wall Exposed to Ordinary Environmental Conditions in a Nuclear Reactor Building: the Contribution of Cement Hydrates and Feldspar Interaction

Long-term Material Properties of a Thick Concrete Wall Exposed to Ordinary Environmental Conditions in a Nuclear Reactor Building: the Contribution of Cement Hydrates and Feldspar Interaction

Reactividad árido-álcali en áridos empleados para hormigón

Reactividad potencial de las rocas andesíticas de Cabo de Gata (SE de España)