Barrier Film of Etherified Hemicellulose from Single-Step Synthesis

Abstract

Hemicellulose with good biodegradability and low oxygen permeability shows great potential in food packaging. However, its strong hydrophilicity leads to its poor moisture resistance, which hinders its wider application. In this paper, a near-hydrophobic hemicellulose was obtained by using single-step synthesis from poplar powder via etherification modification with epoxy chloropropane. This proposed approach has the advantage of avoiding the destruction of hemicellulose structure by secondary alkali-hydrolysis, which was what usually occurred in traditional etherification procedures. The feasibility of using epoxy chloropropane as an alkylation reagent to etherify hemicellulose was confirmed, and the reaction mechanism was elucidated. Contact angle test, thermogravimetric analysis, oxygen transmittance test, and infrared spectrum analysis showed that the barrier property and thermal stability of etherified hemicellulose films have been significantly improved. At an epoxy chloropropane/wood powder ratio (volume/weight) of 2/3 (mL/g), the epoxy hemicellulose films contained the most epoxy groups and displayed the best performance, i.e., tensile strength of 14.6 MPa, surface contact angle of 71.7° and oxygen transmission coefficient of 1.9 (cm3·µm)/(m2·d·kPa), showing great promise as barrier film in food-packaging.

Hydrophobic molecular treatments of cellulose-based or other polysaccharide barrier layers for sustainable food packaging: A Review

“…First, hemicellulose serves as a bonding agent between the fibers in paper products. Second, hemicellulose can be considered as an option for preparing thin films that might be applied onto paper surfaces (Hansen et al 2012;Borjesson et al 2019;Shao et al 2020). Trees commonly used for papermaking have about 25 to 35% of hemicelluloses (Pettersen 1984).…”

“…Shao et al 2020 Urethanes: Molecular Hydrophobic Treatment Conditions, Details, and Water Contact Angles After solvent exchange from acetone to toluene, the nanofibrillated cellulose was reacted with the long-chain isocyanates in the presence of n-butyltindilaurate as a catalyst at 105 °C for 2 h.Cotton linters were reacted with modified castor oil, that had terminal isocyanate groups due to reaction with toluene-di-isocyanate. The final reaction was at 75 °C for 24 h.Both cellulose nanocrystals (CNC) and nanofibrillated cellulose (NFC) were treated with n-octadecyl isocyanate.…”

Nano-SiO2-modified xylan-PVOH-based composite films: Mechanical and barrier properties investigation

“…At a time of increasingly scarce global petrochemical resources and environmental problems caused by the widespread use of petroleum-based materials, the development and utilization of renewable and degradable biomass resources is urgent (Thakur et al 2014;Tayeb et al 2018;Shao et al 2020). Biomass resources are natural energy carriers that store solar energy in the form of chemical energy.…”