Analysis of microstructures for Co/Pd multilayer perpendicular magnetic recording media with carbon underlayer

Perpendicular magnetic anisotropy in Co/Pt multilayers studied from a view point of anisotropy of magnetic Compton profiles

“…The lattice constant of the Co/Pd multilayers and the Co/Pt multilayers obtained from the fcc ͑111͒ reflection have linear relation with the thickness fraction of Co layer. This kind of behavior has been reported on Co/Pd multilayers by Asahi et al 19 These results suggest that the multilayer structure controls the lattice constants of the multilayers.…”

Magnetic Compton profiles of Fe thin film and anisotropy of Co/Pd multilayer

“…This lattice constant is the average value of fcc Pd (aZ0.3890 nm) and fcc Co (aZ0.3545 nm) which is weightened by the atomic ratio. The (111) texture of Co/Pd multilayer has been reported by den Broeder et al [12] and recently Asahi et al [13]. Nakajima et al [14] has suggested that Co has fcc phase with a thickness less than 5 ml in Co/Pt multilayers.…”

Магнитные свойства многослойных пленок Co/Pd на пористых темплатах Al-=SUB=-2-=/SUB=-O-=SUB=-3-=/SUB=- с развитой субструктурой ячеек

“…Кривая симуляции хорошо коррелирует с эксперимен-тальными данными. Данный факт указывает на то, что сплошная пленка, а, следовательно, и пористые системы представляют собой квазисплав CoPd, поскольку более развитая морфология поверхности пористых темплатов приводит к еще более интенсивному перемешиванию слоев осаждаемых на них пленок [31,32]. Полученная из аппроксимации плотность ρ сплава CoPd составля-ет 11.05 g/cm 3 .…”

“…4 представлена теоретическая зависимость изменения постоянной решетки a сплава СoPd по закону Вегарда [31], в зависимости от соотношения количества атомов кобальта n(Co) и палладия n(Pd) в сплаве. На данном рисунке звездочками представлены литературные данные для постоянной решетки Pd [33] и сплава СoPd с гранецентрированной кубической (ГЦК) решеткой и соотношением n(Сo)/n(Pd) = 1 : 1 [34].…”