AgI-Ag2O-V2O5 glasses as ion-to-electron transducers for the construction of all-solid-state microelectrodes

Mamińska, Renata; Kucharek, Marta; Jóźwiak, P.; Garbarczyk, Jerzy E.; Dybko, Artur; Wróblewski, Wojciech

doi:10.1007/s00604-007-0753-8

Cited by 3 publications

(1 citation statement)

References 30 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Amorphous glasses have recently drawn great attention due to the use of oxygen isolation catalysis in fuel cells and cathode material in solid-state devices [1], Superionic oxide glasses in particular are of great importance because they have high thermal stability [2,3]. Many authors have attracted the attention [4][5][6][7][8]studies DC conductivity of semiconducting glasses with composition; AgI-Ag 2 O-B 2 O 3 , AgI-AgPO 3, Ag 2 O-GeO 2 , AgI-Ag 2 O-P 2 O 5 , AgI-Ag 2 O-V 2 O 5 and AgI-Ag 2 O-V 2 O 5 -P 2 O 5 . Otherwise a few reports about photoconductivity studies of oxide glasses containing Ag 2 O, V 2 O 5 are available in the literature.…”

Section: Introductionmentioning

confidence: 99%

Structural and Photoelectronic Features of Novel Vanadate Glass

HEGAZY¹,

ASHRAF²,

ALGARNI³

et al. 2020

JOR

View full text Add to dashboard Cite

A recent vanadate glass within the composition as follows; 50V2O5-30Ag2O- 20SrO was prepared in the mol % through a melt-quenching technique. In this paper, the glass transition,Tg, softening temperature, Ts , and the peak of crystallization, TP, of the present glass determined by using differential thermal analysis (DTA). Moreover, the transient photoconductivity measured at different temperatures in the range 294- 500 K with the intensity of illumination such as; 2000, 3500, 5900, 9400, 13900, 19700, and 26000 lx. The results of dark conductivity 𝜎𝑑 and photoconductivity σph obtained that the conduction mechanism in present glass having two regimes activation energy at the temperature range from 294 to 500 K. The value of σph and 𝜎𝑑 at 297 K was equal 2.604×10-3  -1 ∙ cm-1 and 2.604×10-3  -1 ∙ cm-1 , respectively. Herein the values of activation energy ∆𝐸1𝑝ℎ and ∆𝐸2𝑝ℎ are equal to 0.285 and 0.052 eV for region Ith and II, respectively. Both 𝜎𝑑 and σph increases linearly with a voltage change in the studied range from 0.2 to 5.0 V. The XRDpattern shows a distinct line attributed to the crystalline phase Sr2V2O7 (ICDD card: 00- 048-0145) moreover, the diffraction peaks at 2= 38.3o , 44.5o , and 64.8o are assigned to (111), (200) and (220) peaks of Ag (JCPDS4-0783). The crystallite size of the Ag+ with heat treatment of present glass, which found that equal micro-sized particle 7 m in the glass matrix. Finally, we found that, the 𝜎𝑝ℎ value of the prepared glass is larger than that compared to different glass compositions reported in the literature. Hence the prepared glass is promising as a candidate in optoelectronic devices.

show abstract