A novel etchant for revealing the prior austenite grain boundaries and matrix information in high alloy steels

Cho, K.S.; Sim, Ho Sup; Kim, J.H.; Choi, Joon Hyouk; Lee, K.B.; Yang, Hanry; Kwon, Hoon

doi:10.1016/j.matchar.2007.06.013

Cited by 25 publications

(7 citation statements)

References 14 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…In this way, a difficulty was to reveal prior austenite grain boundaries especially the instability features. It is recently known that most of etching techniques for revealing prior austenite grain boundaries are actually ineffective for severely deformed and highalloyed materials [33]. Fig.…”

Section: Microstructural Observationsmentioning

confidence: 99%

Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps

Momeni

Dehghani

2010

Materials Science and Engineering: A

165

View full text Add to dashboard Cite

Section: Microstructural Observationsmentioning

confidence: 99%

Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps

Momeni

Dehghani

2010

Materials Science and Engineering: A

165

View full text Add to dashboard Cite

“…Andrés et al (2001), citam em seu trabalho o método indireto onde utiliza-se de técnicas metalográficas para observação do antigo contorno de grão austenítico à temperatura ambiente [2]. As técnicas para a revelação do contorno de grão prévio podem ser aplicadas por meio de ataque químico, ataque térmico e por têmpera superficial [2][3][4][5]. No ataque químico, a efetividade do reativo a base de ácido pícrico é controlada pela adição de ácido clorídrico.…”

Section: Introductionunclassified

“…Tem-se a seguinte relação: quanto maior a quantidade de carbono na liga, menor adição de HCl é requerida [3]. Cho et al (2008), ressaltam que o reagente químico baseado em ácido pícrico é muito utilizado para a determinação dos contornos de grão em aços baixa liga. Porém, esse reagente não é satisfatório para tal determinação em aços altamente ligados [4].…”

Section: Introductionunclassified

“…Cho et al (2008), ressaltam que o reagente químico baseado em ácido pícrico é muito utilizado para a determinação dos contornos de grão em aços baixa liga. Porém, esse reagente não é satisfatório para tal determinação em aços altamente ligados [4]. Já o ataque térmico consiste na exposição de amostra de aço polida a temperaturas razoavelmente elevadas, numa atmosfera inerte, promovendo a formação de ranhuras nas interseções dos contornos de grão, permitindo assim a observação dos contornos de grão ao microscópio óptico [6].…”

Section: Introductionunclassified

See 1 more Smart Citation

Avaliação De Diferentes Técnicas De Contraste Para Revelar O Contorno De Grão Austenítico Prévio Em Aços

Moreirar¹,

Faria²,

Fortes³

et al. 2018

ABM Proceedings

View full text Add to dashboard Cite

ResumoA caracterização do tamanho de grão austenítico prévio dos aços é importante, pois a partir desta investigação é possível estimar parâmetros metalúrgicos que repercutirão na qualidade final do produto. Desenvolver métodos para a revelação do contorno de grão prévio se faz necessário, porém, muitas pesquisas apontam para a complexidade destes métodos. Este trabalho se propõe a avaliar diferentes técnicas de contraste para revelar o contorno de grão austenítico prévio dos aços ABNT 1045 e ABNT 4340. Foram utilizadas três técnicas para revelar o contorno de grão austenítico prévio, sendo: ataque químico, ataque térmico e têmpera superficial. Destacam-se o ataque térmico e a têmpera superficial como métodos inovadores. O ataque químico foi realizado em três condições, variando-se a composição de ácido clorídrico adicionado ao reativo a base de ácido pícrico. O ataque térmico foi realizado em duas condições, em atmosfera inerte e em atmosfera oxidante/inerte. A técnica de têmpera superficial consistiu em austenitizar e promover um tratamento térmico de têmpera com restrições na taxa de resfriamento, promovendo um efeito de transformação bainitica nos contornos de grãos austeníticos prévios. Pôde-se concluir que a técnica mais eficiente para os aços estudados foi o ataque químico a base de ácido pícrico. As técnicas de ataque térmico e têmpera superficial se mostraram eficientes para o aço ABNT 1045, apresentando potencial de melhoria metodológica para outros tipos de aços. Palavras-chave: Contorno de grão austenítico prévio; Ataque químico; Ataque térmico; Têmpera superficial. EVALUATION OF DIFFERENT CONSTRAST TECHNIQUES TO REVEAL THE PRIOR AUSTENITE GRAIN BOUNDARY AbstractThe characterization of prior austenite grain boundary of steels are important, because with this parameter knowledge, is possible to estimate metallurgical parameters that could have influence on steel product quality. The development of practical methods aiming to reveal the prior austenite grain boundaries is necessary, but many research papers highlights the complexity of these kind of methods. In this context, this work proposes to evaluate different contrast techniques to reveal the prior austenite grain in ABNT 1045 and ABNT 4340 steels. Techniques as chemical etching, heat etching and surface quenching etching were applied. The heat and surface quenching methods are innovative. The chemical etching was tested in three conditions (HCl content was changed), the heat etching was evaluated in two conditions (inert and oxidizing environment), the surface quenching etching were applied with restrictive conditions in cooling rate, aiming to obtain bainite in prior austenite grain boundaries. It was possible to conclude that the most efficient method is the chemical etching with picric acid and HCl for both studied steel. The heat and surface etching were efficient only for ABNT 1045 steel.

show abstract

“…Uma vez revelados os grãos, seus tamanhos podem ser facilmente medidos [8][9][10][11]. Diferentes métodos para revelação do antigo contorno de grão austenítico têm sido desenvolvidos e podem ser classificados em dois grupos: o primeiro consiste em procedimentos que se baseiam na observação direta da microestrutura austenítica acima da temperatura crítica, fazendo uso de microscopia de alta temperatura [12 e 13]; o segundo usa procedimentos indiretos, nos quais técnicas metalográficas e tratamentos térmicos pós-austenitização são aplicados para revelar os contornos de grãos austeníticos à temperatura ambiente [14,15]. Sabe-se que a sensitização dos contornos de grãos podem ser estimuladas pelo aquecimento das amostras em atmosfera oxidante, e ainda que alguns reativos têm a habilidade de revelar os contornos de grãos austeníticos quando eles contém segregação de alguns elementos químicos, como por exemplo fósforo.…”

Section: Introductionunclassified

Utilização De Um Ataque Por Imersão Na Caracterização Da Influência Da Temperatura E Do Tempo De Austenitização Sobre O Tamanho De Grão Austenítico E Morfologia Da Martensita Em Um Aço Do Tipo Abnt 1045

Martins¹,

Faria²,

Godefroid³

et al. 2014

ABM Proceedings

View full text Add to dashboard Cite

ResumoO tamanho de grão austenítico é um parâmetro que influencia o desempenho de tratamentos térmicos em aços, assim como suas propriedades. Neste contexto, este trabalho investigou o uso de um reativo para ataque por imersão (240ml de água destilada, 2ml de HCl, 2g de ácido pícrico e 5 gotas de detergente neutro) para avaliar a influência da temperatura e do tempo de austenitização sobre o tamanho de grão austenítico de um aço ABNT1045 austenitizado nas temperaturas de 860ºC, 950ºC e 1100ºC por intervalos de tempo de 40, 90 e 180 minutos. As amostras austenitizadas foram temperadas em água, metalograficamente preparadas e atacadas com o reativo proposto com o objetivo de se revelar os antigos contornos de grãos austeníticos. Os tamanhos de grãos foram medidos com a utilização do software UMIAS de forma a possibilitar a determinação de distribuições estatísticas com quinhentas medidas para cada condição de tratamento. As amostras foram novamente preparadas e então atacadas com Nital 2%, sendo possível avaliar a influência do tamanho de grão austenítico sobre a morfologia da martensita. Pôde-se observar que, para o aço ABNT1045, a influência da temperatura de austenitização sobre o tamanho de grão austenítico é muito evidente e mais significativa do que a do tempo. Os valores de tamanho de grão se mostraram exponencialmente dependentes da temperatura, de forma que quanto maior o tamanho de grão austenítico, mais grosseira é a estrutura martensítica e menor é a dureza do material após a têmpera em água. Palavras-chave: Ataque por imersão; Austenitização; Tamanho de Grão; Martensita.

show abstract

A novel etchant for revealing the prior austenite grain boundaries and matrix information in high alloy steels

Cited by 25 publications

References 14 publications

Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps

Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps

Avaliação De Diferentes Técnicas De Contraste Para Revelar O Contorno De Grão Austenítico Prévio Em Aços

Utilização De Um Ataque Por Imersão Na Caracterização Da Influência Da Temperatura E Do Tempo De Austenitização Sobre O Tamanho De Grão Austenítico E Morfologia Da Martensita Em Um Aço Do Tipo Abnt 1045

Contact Info

Product

Resources

About