A karbon aktivitás számításán alapuló diffúziós modell

Abstract

The paper deals with the stability of centerline inhomogenity of the continuously cast slabs. The pattern of the centerline segregation was modeled The paper deals with the stability of centerline inhomogenity of the continuously cast slabs. The pattern of the centerline segregation was modeled physically by preparing a sandwich structure of steel plates with different levels of carbon and alloying elements. The eligibility of sandwich structured samples for diffusional experiments, i.e. the permeability of the metal-metal boundaries in the samples from diffusional point of view was checked by the comparison of measured and theoretically calculated hardness value for plain carbon steels. Diffusional homogenization experiments were performed and the samples were examined metallographically. The paper deals with the details of mathematical approach including the cross effects between carbon and manganese during the diffusional process. ÖsszefoglalásEz a fejezet a már létrejött középvonali dúsulás természetével, illetve a dúsulás csökkentésének lehetőségével foglalkozik. A középvonali szegregáció a lemezbuga hengerlése során elnyúlik, a durvalemezek és sokszor a tekercselt szalagok középvonalában is kimutatható. Ez a jelenség a feldolgozás során elsősorban a durvalemezek esetében jelent problémát (rétegesség, hegesztési, alakítási nehézségek). Általános tapasztalat, hogy a lemezbugában kialakult középvonali szegregáció a hengerlést követően a durvalemezek utólagos hőkezelésével alig mérsékelhető. A kutatási munka során arra a kérdésre kerestük a választ, hogy milyen tényezők, milyen mechanizmussal befolyásolják a középvonali szegregáció stabilitását. A dolgozat a karbon és mangán közötti kölcsönhatást is magában foglaló diffúziós modell matematikai leírásával foglalkozik.