Curvas de correlação para caracterizar concretos usados no Rio de Janeiro por meio de ensaios não destrutivos

Abstract

ResumoNon-destructive tests give information about the properties of the concrete of a structure, but the reliability of the evaluation of those properties depends on the experience of the professional that carries out the tests and the curves employed to correlate the measured values with the properties of the investigated concrete. The main objective of this study was to supply engineers with correlation curves that make it possible to evaluate, by using non-destructive test results, the compressive strength and the modulus of elasticity of ready-mixed concretes used in Rio de Janeiro. Test specimens cast with concretes used in several constructions and supplied by different ready-mixed concrete producers were tested. These concretes had, in general, nominal fck value of 25 MPa or 30 MPa. Aiming to include concretes with strength varying within a wider range and made with the two types of typical coarse aggregates of Rio de Janeiro, test specimens cast in the laboratories of two readymixed concrete producers were tested. In these concretes, the water-cement ratio (0.40 to 0.60) and the petrographic characteristic of the coarse aggregate were varied. Compressive strength and modulus of elasticity tests, ultrasonic pulse velocity, rebound hammer and penetration resistance tests were carried out, at the ages of 3, 7, 14, 28 and 90 days. The correlation curves obtained from the analysis of the results of all those tests are presented here. When only one non-destructive test was used, the rebound hammer was the one that led to the best estimation of compressive strength and the combination of that test with the penetration resistance test improved the accuracy of the evaluation. If modulus of elasticity tests cannot be carried out, the ultrasonic pulse velocity test can be an interesting option to evaluate that property. Keywords: correlation curves, nondestrutive tests, ready-mixed concreteOs ensaios não destrutivos fornecem informações quanto às propriedades do concreto das estruturas, mas a confiabilidade da avaliação dessas propriedades depende da experiência do profissional que realiza esses ensaios e das curvas empregadas para correlacionar as grandezas medidas nos ensaios com as propriedades do concreto investigado. Este estudo visou prover os engenheiros de curvas de correlação que os possibilitem estimar, por meio da utilização de ensaios não destrutivos, a resistência à compressão e o módulo de elasticidade dos concretos dosados em central utilizados no Rio de Janeiro. Foram ensaiados corpos-de-prova moldados com concretos usados em diversas obras, fornecidos por diferentes concreteiras. Esses concretos tinham, em geral, fck nominal de 25 MPa ou 30 MPa. Objetivando englobar concretos com resistências mais variadas e os dois tipos de agregados graúdos típicos do Rio de Janeiro, foram ensaiados corpos-de-prova moldados nos laboratórios de dois grupos de concreteiras. Nestes concretos, variaram-se a relação água-cimento (0,40 a 0,60) e a característica petrográfica do agregado graúdo. Foram realizad...

Curvas de correlação para caracterizar concretos usados no Rio de Janeiro por meio de ensaios não destrutivos

“…Tests were done with 10 types of curve [12] for each correlation, with the choice being made for those that showed the greatest coefficient of determination (R 2 ). The expressions proposed for the 3 combined methods studied here are shown in Table 5.…”

“…In these concretes the variables were the water-cement ratio (0.40, 0.45, 0.50, 0.55 and 0.60) and the petrographic characteristic of the coarse aggregate (crushed granitic gneiss and syenite). The composition of the concretes of this stage is presented by Machado [12]. The following tests were carried out, both in the 1 st as in the 2 nd stage: compressive strength tests and ultrasonic pulse velocity, rebound hammer and penetration resistance tests.…”

“…The criterion used in establishing this new limit, described in detail by Machado [12], consisted of considering the average of only 3 L e values from the 4 obtained, discarding the one that showed the greatest difference in relation to the average value of the 4 obtained. The differences between the L e value of the excluded probe and the greatest or smallest L e value of the remaining 3 probes showed that the value recommended by BS 1881:Part 207 [10], 5mm, was more adequate to use in the analysis of the tests undertaken in this work.…”

Utilização de Ensaios Não Destrutivos, Ultrassom e Pacômetro, como Métodos de Verificação da Resistência e Qualidade do Concreto em um Edifício em Aracaju – Sergipe

“…[7] Assim sendo, para que os métodos de ensaio in situ sejam utilizados para avaliar a resistência do concreto, são necessárias curvas de correlação entre os resultados destes ensaios e a resistência à compressão do concreto. Complementando ainda sobre fatores que contribuem com a durabilidade de uma construção, o cobrimento é um fator de suma importância.…”

Análise do estado de conservação do Monumento a Ramos de Azevedo com utilização de métodos não destrutivos

“…da força compressiva uniaxial (UCS) e do módulo de Young (E). No entanto, microfraturas de esmagamento de grãos e colapso de poros pode ocorrer em rochas friáveis e porosas, exigindo a utilização de diferentes amostras.Alta velocidade de execução, baixo custo, ausência de danos significativos, possibilidade de coleta de grande quantidade de dados, dados disponíveis de maneira imediata, sem necessidade da coleta de amostras, são algumas das vantagens do método(Machado, 2005).Esmagamento de grãos soltos devido ao estado da face ensaiada, movimento do bloco e estado físico do instrumento são alguns motivos que levam a obtenção de resultados baixos em campo. No entanto, nem todos os valores baixos podem ser atribuídos a essas razões, pois as rochas não são perfeitamente homogêneas, o que resulta em algumas variações dos resultados durante o teste.…”