Characterization of aqueous silver nitrate solutions for leakage tests

Abstract

ObjectivesTo determine the pH over a period of 168 h and the ionic silver content in various concentrations and post-preparation times of aqueous silver nitrate solutions. Also, the possible effects of these factors on microleakage test in adhesive/resin restorations in primary and permanent teeth were evaluated.Material and MethodsA digital pHmeter was used for measuring the pH of the solutions prepared with three types of water (purified, deionized or distilled) and three brands of silver nitrate salt (Merck, Synth or Cennabras) at 0, 1, 2, 24, 48, 72, 96 and 168 h after preparation, and storage in transparent or dark bottles. Ionic silver was assayed according to the post-preparation times (2, 24, 48, 72, 96, 168 h) and concentrations (1, 5, 25, 50%) of solutions by atomic emission spectrometry. For each sample of each condition, three readings were obtained for calculating the mean value. Class V cavities were prepared with enamel margins on primary and permanent teeth and restored with the adhesive systems OptiBond FL or OptiBond SOLO Plus SE and the composite resin Filtek Z-250. After nail polish coverage, the permanent teeth were immersed in 25% or 50% AgNO3 solution and the primary teeth in 5% or 50% AgNO3 solutions for microleakage evaluation. ANOVA and the Tukey's test were used for data analyses (α=5%).ResultsThe mean pH of the solutions ranged from neutral to alkaline (7.9±2.2 to 11.8±0.9). Mean ionic silver content differed depending on the concentration of the solution (4.75±0.5 to 293±15.3 ppm). In the microleakage test, significant difference was only observed for the adhesive system factor (p=0.000).ConclusionsUnder the tested experimental conditions and based on the obtained results, it may be concluded that the aqueous AgNO3 solutions: have neutral/alkaline pH and service life of up to 168 h; the level of ionic silver is proportional to the concentration of the solution; even at 5% concentration, the solutions were capable of indicating loss of marginal seal in the composite restorations; the 3-step conventional adhesive system had better performance regarding microleakage in enamel on primary and permanent teeth.

Evaluation of microleakage in class V composite restorations using dye penetration and micro-CT

“…In general, the results of the current study showed significantly higher microleakage values in dentin than in enamel using the different etch and rinse adhesives, which agrees with other studies [7,25,34].…”

“…The use of silver nitrate has been favored in microleakage laboratory studies because other dyes (such as fuchsin or methylene blue) tend to wash out during sectioning of the specimens [33]. Costa et al showed that the effectiveness of ionic silver is proportional to the concentration of the solution; even at a concentration of 5 %, the solutions were capable of indicating loss of marginal seal of composite restorations [34]. A 50 wt% ammoniacal silver nitrate solution was used in this study to measure dye penetration because this procedure has proven to be an acceptable method in dental research and allows the comparability of this study to other in vitro studies [35].…”

An in vitro microleakage evaluation of class V cavities restored with silorane-based resin composite using different adhesive systems

“…However, this adhesive system still has the characteristics similar to the conventional adhesive systems, especially regarding to its mechanism of bonding to the enamel and dentine. The adhesive system of the silorane-based composites little differs from a common 2-step self-etch adhesive system, including the application of two resin solutions: an essentially hydrophobic primer to bond to the dental tissue; and a hydrophobic adhesive to bond appropriately the dental substrate previously conditioned by the primer to the hydrophobic composite [14].…”

Avaliação clínica e ex vivo de molares decíduos submetidos a diferentes protocolos terapêuticos no manejo da cárie dentária

“…Inúmeras metodologias têm sido empregadas para avaliação do selamento marginal de restaurações, sendo a penetração de corantes e marcadores químicos uma das mais difundidas, por permitir a sua detecção em contraste aos tecidos dentários e aos materiais restauradores empregados sem a necessidade de uso de 69 materiais radioativos (67,97 instrumentos manuais e restauradas com cimento de ionômero de vidro de alta viscosidade e; iii) tratamento ultraconservador (UCT), que consistiu em uma combinação da abordagem ART, para restaurar cavidades de pequeno porte, com a remoção diária do biofilme dental com uso de escova de dentes e creme dental nas 70 cavidades de médio e grande portes (89). Por se tratarem de dentes decíduos, cuja esfoliação era esperada, uma análise ex vivo pôde ser conduzida, permitindo a avaliação de características químicas e mecânicas dos materiais aplicados, tal como a presença de microfraturas marginais das restaurações implementadas.…”

“…Em contrapartida, restaurações que empregam cimentos de ionômero de vidro (CIV), como as realizadas por meio da técnica do Tratamento Restaurador Atraumático (ART), se aderem quimicamente aos tecidos dentários, sendo esta a possível razão para a baixa prevalência de cárie secundária associada a restaurações de ionômero de vidro (96). Entretanto, apesar dessa adesão físico-química e da melhora nas propriedades dos cimentos de ionômero de vidro observada nas últimas décadas, ainda é possível notar uma taxa considerável de falha de restaurações ART de múltiplas superfícies, sendo importante avaliar se o sucesso clínico dessas restaurações está associado ou não à presença de microinfiltrações marginais, comparando-as a tratamentos convencionais.Inúmeras metodologias têm sido empregadas para avaliação do selamento marginal de restaurações, sendo a penetração de corantes e marcadores químicos uma das mais difundidas, por permitir a sua detecção em contraste aos tecidos dentários e aos materiais restauradores empregados sem a necessidade de uso de 69 materiais radioativos (67,97 instrumentos manuais e restauradas com cimento de ionômero de vidro de alta viscosidade e; iii) tratamento ultraconservador (UCT), que consistiu em uma combinação da abordagem ART, para restaurar cavidades de pequeno porte, com a remoção diária do biofilme dental com uso de escova de dentes e creme dental nas 70 cavidades de médio e grande portes (89). Por se tratarem de dentes decíduos, cuja esfoliação era esperada, uma análise ex vivo pôde ser conduzida, permitindo a avaliação de características químicas e mecânicas dos materiais aplicados, tal como a presença de microfraturas marginais das restaurações implementadas.…”