Difference in the color stability of direct and indirect resin composites

Abstract

Indirect resin composites are generally regarded to have better color stability than direct resin composites since they possess higher conversion degreeObjectiveThe present study aimed at comparing the changes in color (∆E) and color coordinates (∆L, ∆a and ∆b) of one direct (Estelite Sigma: 16 shades) and 2 indirect resin composites (BelleGlass NG: 16 shades; Sinfony: 26 shades) after thermocycling.Material and MethodsResins were packed into a mold and light cured; post-curing was performed on indirect resins. Changes in color and color coordinates of 1-mm-thick specimens were determined after 5,000 cycles of thermocycling on a spectrophotometer.Results∆E values were in the range of 0.3 to 1.2 units for direct resins, and 0.3 to 1.5 units for indirect resins, which were clinically acceptable (∆E<3.3). Based on t-test, ∆E values were not significantly different by the type of resins (p>0.05), while ∆L, ∆a and ∆b values were significantly different by the type of resins (p<0.05). For indirect resins, ∆E values were influenced by the brand, shade group and shade designation based on three-way ANOVA (p<0.05).ConclusionDirect and indirect resin composites showed similar color stability after 5,000 cycles of thermocycling; however, their changes in the color coordinates were different.

Short and long term effects of additional post curing and polishing systems on the color change of dental nano-composites

“…Moreover, the composition and volume of organic matrix, type and volume of filler particles, type of filler-matrix silanization, and polishing have been reported as the relevant factors in the composite susceptibility to staining 4) . Color stability of resin composites has been reported as being improved when materials showed low water sorption, high fillerresin ratio, reduced particle size and hardness and an optimal filler-matrix coupling system 9) . Previously, nano-composites have been claimed to combine the good mechanical strength of the hybrid-type composites 10,11) and the superior polish of the microfills 12) .…”

Termal siklusun indirekt kompozit rezin materyallerinin renk stabilitesi üzerine etkisi

“…26 Benzer şekilde, termal siklusa bağlı oluşan bu ayrışma, su absorbsiyonu, ve lekelenme, kompozit rezinlerde renk değişiklikleri oluşturmaktadır. 19 Matsumura ve ark. 27 artık monomer miktarının renk stabilitesinde etkili olduğunu ifade etmişlerdir.…”

“…19 indirekt kompozit rezinlerde 5000 termal siklus sonrası oluşan renk farklılıklarını karşılaştırmışlar ve renk değişiminin (∆E) 0.3-1.5 arasında olduğunu göstermişlerdir, ancak bizim çalışmamızdan farklı olarak, Lee ve ark. 19 farklı indirekt kompozit rezinleri test etmişler ve rezin polimerizasyonu için ikinci bir polimerizasyon uygulamışlardır. Önceki çalışmalarda ikinci polimerizasyon sonrası artan karbon çift bağlarının renk stabilitesini arttırdığı bildirilmiştir.…”

“…Bu sonuçlar, her bir materyalin içerdiği farklı doldurucu tip/miktarı ve matriks yapısın-dan kaynaklanabilir. 19 Geurtsen ve ark. 23 hibrit materyallerin yüksek organik matriks içeriklerinden dolayı daha yüksek su absorbsiyon ve materyal ayrışması gö-sterdiklerini bildirmişlerdir.…”

“…Bu nedenle ağız içini iyi bir şekilde yansıtan termal siklus işlemlerinde standart koşulların ileri çalışmalarda araştırılarak sağlanması gerekmektedir. 19,25,33,34 …”