A continuum damage model for the stress corrosion cracking of austenitic stainless steel

Abstract

In the present work, the mechanical behavior of stress corrosion cracking phenomenon is described. Such

A continuum damage mechanics model for pit-to-crack transition in AA2024-T3

“…We followed this approach in this paper. Da Costa-Mattos et al [36][37][38][39] presented a CDM model for SCC damage that includes environmental parameters. The model accounts for stress corrosion damage through reduction of mechanical resistance of material.…”

“…The model in Eq. (4) is merely applied to SCC by da Costa-Mattos et al [36][37][38][39]. It's applicability to pitting CF, however, is not explored.…”