Glass-ceramic produced with recycled glass

Abstract

The objective of this work is the production and characterization of glass-ceramic with recycled glass powder and 4% (w/w) of cerium dioxide. Eleven groups were defined with conformation pressure of 11.6 and 25.8 MPa, and cerium dioxide addition. The sintering temperatures of 650, 675, 700 and 750 °C were used. The raw material was formed into a mold with a uniaxial pressure. The density was measured by the Archimedes principle. The water absorption of the groups was also determined, as linear contraction percentage and the crystalline structure. The flexural strength was obtained by the three-point bending test and the results analyzed by the Weibull analysis. The specimens presented density ranging from 1.99 to 2.38 g/cm3. Increasing the temperature provided an increase in the density of the specimens and the flexural strength. At higher sintering temperature, this behavior was not observed. The highest flexural strength was 63.55 MPa, obtained at the sintering temperature of 700 ºC, conformed with 25.8 MPa, only glass powder. The increase in the forming pressure favored crystallization. The addition of cerium dioxide favored for the increase density and the Weibull modulus, but decrease of the flexural strength.

Medida da solubilização de cloreto de magnésio em solução aquosa por condutividade do eletrólito

“…Na prensagem, os grãos de sal não ocupam todo o volume, assim a pastilha é constituída por uma fração sólida e de espaços vazios, os poros. A maior parte dos poros é fechada, ou seja, os poros não estão conectados com a superfície da pastilha [6], no entanto, existem alguns que são abertos e, com isso, possuem conexão com a superfície. Ao começar o processo de dissolução as camadas mais externas de sal, que estavam impedindo que o ar aprisionado dentro dos poros saísse, se dissolvem liberando gradativamente bolhas, que por sua vez, agitam o meio.…”

Recycled Bottle Glass Wastes as Precursors for Porous Alumina Glass Ceramics Synthesis

“…The civil and construction industries use recycled glass as aggregates for architectural concrete [8][9][10], pavements [11] and road construction material [12]. New glass ceramic materials having good thermal, mechanical, chemical, biological and dielectric properties can be synthesized using recycled glass [13][14][15]. The glass powder obtained by mechanical crushing can replace the sodium silicate in manufacturing geopolymers, based on its' high amount of silica [16,17].…”

Reciclagem e a Engenharia de Superfícies

“…O destino de resíduos sólidos urbanos tem sido tema de inúmeras pesquisas recentes [1] e a incineração de resíduos ainda é um processo eficiente em termos de aproveitamento energético. Mas nos últimos anos, tem havido um esforço em se pesquisar novas aplicações para resíduos sólidos urbanos e, neste número 4 do volume 24 da revista Matéria, temos exemplos destas pesquisas como a produção de cerâmica vítrea com vidro reciclado [2] e a adição de resíduo de vidro em massa de cerâmica de alvenaria [3]. Nesta edição, é descrito o emprego de cenosferas, sub-produto da combustão do carvão, na substituição parcial à areia para a produção de materiais cimentícios de baixo peso [4].…”