Fabrication of a new porous glass-ceramic monolith using vanadium(III) calcium phosphate glass as precursor

Abstract

Resultados preliminares de XRD, IR, Raman e SEM mostraram que monólitos vitrocerâmicos porosos (pgc-LVCP) com esqueleto tridimensional constituído pelas fases V(PO 3 ) 3 e Ca 3 (VO 4 ) 2 foram obtidos utilizando um vidro original de Li 2 O-V 2 O 3 -CaO-P 2 O 5 como precursor. O pgc-LVCP pode ser um hospedeiro poroso promissor para sistemas químicos integrados visto que a fase Ca 3 (VO 4 ) 2 apresenta propriedades ferroelétricas e de luminescência enquanto a fase V(PO 3 ) 3 exibe propriedades magnéticas associadas com elevada estabilidade mecânica, química e térmica.Preliminary XRD, IR, Raman and SEM data indicate that porous glass-ceramic monoliths (pgc-LVCP) with skeleton of V(PO 3 ) 3 and Ca 3 (VO 4 ) 2 with three-dimensional network structure using an original Li 2 O-V 2 O 3 -CaO-P 2 O 5 glass as precursor was obtained. The pgc-LVCP is a promising porous host for integrated chemical systems because the Ca 3 (VO 4 ) 2 has ferroelectric and luminophor properties while V(PO 3 ) 3 exhibits magnetic properties associated with high degree of mechanical, chemical and thermal stability.

Electronic structure and luminescence assets in white-light emitting Ca2V2O7, Sr2V2O7 and Ba2V2O7 pyro-vanadates: X-ray absorption spectroscopy investigations

“…These bands are mainly due to the stretching vibrations of metal-oxygen bonds and bending vibrations of VO 4 3À groups in triclinic structured A 2 V 2 O 7 pyrovanadates. 29,30 The v4 and v3 bands are the results of V-O-V bridge vibration and asymmetric stretching of longer V-O bond. 31,32 The rest of the bands (v1 and v2) can be ascribed to symmetric stretching of the other shorter V-O bonds in the samples.…”

Crystal structure and photoluminescent properties of BaZn1−Eu V2O7 nanoparticles

“…The frequency bands originating at 1600 cm À1 and 3400 cm À1 attributed to bending and stretching modes of water molecules due to adsorbed moisture by the powder are absent due to volatilization of H 2 O at high temperature. The absorption bands in the range 500e1025 cm À1 are assigned to stretching and bending vibrations of the VO 4 3À group [31,32]. The IR bands in the region 1020e740 cm À1 owing to VeO stretching vibrations while the band at 506 cm À1 owing to VeO stretching vibrations are observed.…”

Estudo por espectroscopia micro-Raman dos mecanismos de separação de fase em vidros fosfatos de metais de transição

“…[15][16][17] A separação de fases cristalinas em vidros, induzida por irradiação com lasers, é outra linha bastante representativa do uso da espectroscopia micro-Raman ao estudo de sistemas vítreos multifási-cos. [18][19][20] A grande vantagem neste último caso é a formação das fases cristalinas restrita à superfície dos vidros, com morfologia controlada, que pode ser caracterizada com precisão com a espectroscopia microRaman. Por outro lado, a determinação dos mecanismos de separação de fases em vidros é uma possibilidade ainda inexplorada, diante do grande potencial da técnica.…”