Efeito da adição de Na2O na viscosidade e devitrificação do vidro obtido a partir de cinzas volantes e Li2O

Neves, Etney; Poffo, Edoardo D.; Fredel, Márcio C.; Riella, Humberto Gracher; Alarcon, Orestes Estevam

doi:10.1590/s0100-40421998000400031

Cited by 4 publications

(1 citation statement)

References 0 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Esto facilita el cálculo porque es suficiente conocer la viscosidad a dos temperaturas. Se utilizó un dilatómetro (Adamel-Lhomargy, modelo DI-24) para determinar la temperatura de transición vítrea T g y un microscopio de calefacción (Misura HSM, modelo M3M 1600.80.2) para cuantificar la temperatura de semiesfera T s2 , temperaturas a las cuales se asume que la viscosidad es 10 12 Pa·s y 10 3.5 Pa·s respectivamente (19,20). En la tabla II se muestran los resultados obtenidos.…”

Section: Viscosidadunclassified

Modelización mecánica del enfriamiento rápido en sistemas tipo gres porcelánico

Bó¹,

Soler²,

Sánchez-Vilches³

et al. 2012

Bol. Soc. Esp. Ceram. Vidr.

View full text Add to dashboard Cite

En este trabajo se analiza el efecto del enfriamiento sobre el comportamiento mecánico y, en particular, sobre las tensiones residuales que aparecen cuando se trabaja con materiales tipo gres porcelánico. Estas composiciones tienen una microestructura muy compleja, donde se encuentran varias fases cristalinas y la fase vítrea dista de ser homogénea. Por ello se planteó trabajar con una composición más sencilla, empleando como material de partida feldespato sódico al que se añadió cuarzo de diferente tamaño de partícula. Se utilizó un modelo viscoelástico para la estimación de las tensiones residuales que se producen durante el enfriamiento. Los parámetros del modelo se obtuvieron de la bibliografía o se determinaron en ensayos de laboratorio. Se diseñó un montaje que permitía la medida sin contacto de la temperatura en las superficies superior e inferior de la pieza durante el enfriamiento. Las probetas fueron sometidas a diferentes tipos de enfriamientos y, a continuación, se determinaron las tensiones residuales mediante el método de relajación de las deformaciones por corte. Palabras clave: tensiones residuales, viscoelasticidad, modelización, enfriamiento, resistencia mecánica. Mechanical modelling of rapid cooling in porcelain tile-type systemsThis paper analyses the effect of cooling on mechanical behaviour, in particular, on the residual stresses that appear when materials of the porcelain tile type are involved. However, these compositions have a very complex microstructure, in which there are several crystalline phases and the glassy phase is not homogeneous. In this study a simpler composition was therefore formulated, using sodium feldspar as starting material to which quartz with different particle sizes was added. A viscoelastic model was used to estimate the residual stresses that develop during cooling. The parameters of the model were obtained either from the literature or were determined in laboratory tests. An assembly was designed that allowed non-contact measurement of the temperature at the top and bottom surfaces of the test pieces during cooling. The test pieces were subjected to different types of cooling and their residual stresses were then determined by the strain relaxation slotting method.Keywords: residual stresses, viscoelasticity, modelling, cooling, mechanical strength. IntroduccIónEs bien conocido que, en piezas cerámicas, el enfriamiento rápido conduce a tensiones residuales en las piezas a la salida del horno. Esto sucede incluso con productos que generan poca fase vítrea a elevada temperatura (revestimiento poroso). Las tensiones residuales son importantes porque influyen sobre:• La resistencia mecánica de las piezas.• Las curvaturas en diferido, aunque éstas dependen mucho de la fluencia del material. • El proceso de corte durante la instalación de las baldosas.Las tensiones residuales pueden hacer que las piezas se corten según trayectorias no deseadas, o que se rompan.• En el rectificado, la eliminación de zonas tensionadas puede provocar un cambio de curvatura. Vol 51, 2,...

show abstract

Section: Viscosidadunclassified