Formulation and characterization of antibacterial orthodontic adhesive

Abstract

Objective: The objective of this study was to formulate experimental orthodontic bracket adhesives and test their mechanical properties, fluoride release and antibacterial activity. Methods: Four experimental antibacterial orthodontic bracket adhesives were prepared with different compositions of synthesized antibacterial monomers replacing total 5% of dental monomers in the control Transbond XT (3M): 5%C11, 3.5%C11+1.5%C2, 5%C16, and 3.5%C16+1.5%C2. Transbond XT alone was used as control. These groups were used to bond premolar brackets to extracted premolars. Shear bond strength (SBS) was tested using an Instron machine. For antibacterial test, disk specimens (10mm diameter, 1mm thick, n=4) were fabricated and incubated with cultures of cariogenic Streptococcus mutans for 48h, and following gentle sonication, S. mutans biofilms in colony-forming-units (CFU) on the disks were enumerated by plating on agar medium. The data were analyzed using ANOVA and Tukey test (α=0.05). Results: All experimental groups had similar shear bond strength (no significant difference) to the control. All experimental groups showed significant inhibitory effect against S. mutans biofilm formation, when compared to the control, but there was no significant difference between experimental groups. Conclusion: Antibacterial orthodontic adhesive can be fabricated to have similar mechanical properties but better caries-inhibitory effect than current adhesive.

Actividad Antibacteriana de una Resina Ortodóntica Modificada con Diferentes Concentraciones de Nanopartículas de Óxido de Cobre

“…Adicionalmente en este estudio se realizó el análisis de las UFC, todas las concentraciones de NPOCu mostraron un conteo significativamente menor de UFC que las generadas en el grupo control, para las dos cepas estudiadas. No existen reportes que empleen esta metodología para evaluar el efecto del agregado de las NPOCu en resinas ortodónticas, sin embargo, se ha utilizado con nanopartículas de plata, demostrando ser una metodología útil para evaluar el efecto antibacteriano frente a diversas bacterias cariogénicas (Sodagar et al;Twomley et al, 2019). Los resultados mostraron una relación inversamente proporcional entre la disminución del conteo de UFC y el incremento de la concentración de NPOCu.…”

Evaluación de la adhesión de sistemas adhesivos de grabado total en esmalte dental bovino usando un agente desproteinizante: un estudio <i>in vitro</i>

“…10,11 Por otro lado, se ha reportado que el sistema adhesivo OrthoSolo seguido de la resina compuesta Enlight, ambos de la casa comercial ORMCO, pueden ofrecer valores de resistencia al desalojo adecuados para tratamientos ortodóncicos que van de los 9.79 a los 20.83 MPa, 12 mientras que el sistema adhesivo Transbond XT de la casa comercial 3M ofrece valores de adhesión alrededor de 10.23 MPa. 13 Nuestro estudio encontró que el uso de un agente desproteinizante durante 60 segundos previo al grabado ácido aumenta la adhesión en esmalte (p < 0.05). Al comparar los sistemas adhesivos se obtuvieron resultados estadísticamente significativos que demostraron que la resina de ORMCO tenía una mayor fuerza de unión al esmalte que la de 3M (Figura 1B), pero también, nuestros resultados indicaron que la presencia del agente desproteinizante y la marca 3M tienden a incrementar los valores de resistencia al desalojo.…”

Sustained antibacterial activity of orthodontic elastomeric ligature ties coated with a novel kombucha-derived bacterial nanocellulose: An in-vitro study

“…To reduce the risk of enamel decalcification and overcome the above-mentioned non-adherence by the patients, it has been suggested to coat the elastomeric ligatures with antimicrobial materials to provide a sustained and adequate dose of antibacterial delivery. In this regard, the use of fluoride, silver nanoparticles, and chlorhexidine hexametaphosphate has been investigated [ 10 , 12 , 13 , 17 ].…”