Histological analysis of the use of biphasic ceramics based on hydroxyapatite and β-tricalcium phosphate in maxillary sinus floor elevation surgery: pilot study

Abstract

Objective To evaluate the bone repair associated with the use of biphasic ceramics based on hydroxyapatite and β-tricalcium phosphate (HA/TCP) in the procedures of maxillary sinus membrane elevation in human beings. Material and method Ten patients with a residual bone ridge in the posterior maxillary region between 3 mm and 5 mm in height were selected and indicated for procedures of bone grafting associated with maxillary sinus lift procedure. The maxillary sinuses were filled with HA/TCP, and after 8 months, the implants were implanted and a bone biopsy was collected with the aid of a trephine drill, which was then submitted to histological analysis for the evaluation of the composition of the grafted area. Result The histological description analysis of the biopsies revealed the presence of vital and immature bone tissue, juxtaposed to the biomaterial. Histomorphometric analysis showed that the biopsy composition was in average 28.8%, 27.4%, and 43.6% of bone tissue, biomaterial, and soft tissue, respectively. Conclusion The areas grafted with HA/TCP presented the adequate amount of bone formation that allowed the implantation of the implants. The success of the grafting procedure with this biomaterial was associated with its osteoconduction potential that allowed the formation of bone tissue in close contact with HA/TCP.

Plant Extracts in the Bone Repair Process: A Systematic Review

“…However, inflammatory and histopathological analyses play an important role in helping to interpret and confirm the cellular action of phytotherapeutic compounds in tissue repair [73]. The action of osteogenic cells on bone callus formation, cell organization, and the release of immunomarkers is a factor that can be confirmed by histology and immunohistochemistry [74–76], thus leading the experiment to a greater reliability of its results. The synthesis of proinflammatory mediators, in regions of spongy bone and compact bone, indicated in immunological and histopathological analyses, was higher in the phytotherapeutic treatment groups when compared to the control groups, demonstrating an efficiency of extracts in bone repair.…”

Análise comparativa entre os enxertos autógeno e beta fosfato tricálcio associado à hidroxiapatita no tratamento de levantamento de seio maxilar: revisão de literatura

“…Em estudo realizado utilizando dez pacientes como amostra, o qual avaliou de forma qualitativa do uso da cerâmica bifásica a base de HA e BFT no tratamento no levantamento de seio maxilar por meio de inspeções histológicas, relatou-se que nos cortes analisados, o biomaterial apresentava osso maduro, saudável e presença de células multinucleadas nas áreas de reabsorção. Nenhum processo inflamatório foi observado e a formação de tecidos moles entre a superfícies ósseas e do biomaterial não foi relatada (Padovan et al, 2018).…”

“…A análise histofotométrica apresentou porcentagens que se diferenciaram em quantidade de tecidos moles e mineralizados na área enxertada, totalizando em 28,8% de tecido ósseo, 27,4% do biomaterial e 43,6% de tecido mole durante o período analisado. Outrora, foi observado após oito meses da realização do tratamento, que o osso autógeno apresentou maior quantidade de osso formado em 36,8%, mas este não foi um fator determinante para os resultados clínicos positivos do estudo (Padovan et al, 2018).…”

“…Ademais, foi possível observar que as partículas do biomaterial estavam rodeadas por osso vital com pouca presença de células inflamatórias e após nove meses da realização da elevação da membrana, foi observado que ambos os enxertos foram suficientes para a viabilização do leito receptor para colocação de implantes, sendo assim, um biomaterial seguro no tratamento de levantamento de seio maxilar (Padovan et al, 2018).…”