Long-term bond strength of a self-adhesive resin cement to intraradicular dentin pretreated with chlorhexidine and ethanol

Abstract

ResumoIntrodução: Cimentos resinosos autoadesivos não necessitam de tratamento prévio da superfície dental, por esta razão o pré tratamento da dentina pode influenciar a longevidade da resistência adesiva. Objetivo: Avaliar a influência do tratamento dentinário com etanol (ET) 100% e clorexidina (CL) 2% na resistência de união (RU) de um cimento resinoso autoadesivo (CRA) à dentina intrarradicular. Material e método: 80 raízes bovinas restauradas com pino de fibra de vidro e CRA (U200 3M/ESPE) foram distribuídas em 4 grupos, de acordo com o tratamento prévio da dentina intrarradicular: Grupo 1 -nenhum tratamento; Grupo 2 -CL2% por 1 minuto; Grupo 3 -ET100% por 1 minuto; Grupo 4 -CL2% seguido pelo ET100%. As amostras foram seccionadas no sentido radial para obtenção de duas secções de aproximadamente 0,7 mm de espessura em cada terço -cervical, médio e apical. Após 48 horas e 180 dias foi realizado o teste push-out. Resultado: A ANOVA a três critérios para blocos casualizados demostrou que não houve diferença entre os valores de resistência de união nos tempos 48 h e 180 dias, independentemente do tratamento e do terço (p>0,05). A interação tratamento-terço foi significativa (p = 0,041) sendo que o tratamento com CL promoveu menor RU no terço cervical e o tratamento com ET promoveu melhor RU no terço apical. Conclusão: Os tratamentos com CL e ET individualmente ou associados não promoveram diferenças entre os valores de RU do CRA à dentina intrarradicular ao longo do tempo.Descritores: Etanol; clorexidina; técnica para retentor intrarradicular; cimentos de resina. AbstractIntroduction: Self-adhesive resin cements do not require prior preparation of the tooth surface, therefore dentin pretreatments may influence long-term bond strength. Objective: To evaluate the influence of 100% ethanol (ET) and 2% chlorhexidine (CL) treatment of intraradicular dentin on the long-term bond strength (BS) of a self-adhesive resin cement (SRC). Material and method: 80 bovine roots were restored with fiber posts and SRC (U200 3M/ESPE) and distributed into 4 groups according to dentin treatment: Group 1 -without treatment; Group 2 -2% CL for 1 minute; Group 3 -100% ET for 1 minute; Group 4 -2% CL, followed by 100% ET. The samples were cross-sectioned to obtain two sections (0.7 mm) thick for each root third: coronal, middle and apical. The immediate push-out test was carried out after 48 hours, and the long-term push-out test, after 180 days. Result: The three-way ANOVA test for randomized blocks showed no difference between the BS values at 48 hours and 80 days, irrespective of the treatment and the third (p>0.05). The interaction of the treatment/third pairing was significant (p = 0.041) since the treatment with CL promoted lower BS in the coronal third, while treatment with ET promoted better BS in the apical third. Conclusion: Treatment with CL and ET, separately or combined, promoted no differences between the BS values of the SRC to root dentin over time.

Influence of different intraradicular chemical pretreatments on the bond strength of adhesive interface between dentine and fiber post cements: A systematic review and network meta‐analysis

“…The main characteristics of the 61 selected in vitro studies are presented in Table S2 [10, 11, 15–19, 21–30, 34, 35, 38–78]. Human teeth were used in most of the studies ( n = 40), of which 6 studies used posterior teeth, 31 used anterior teeth, and 24 reported using only single‐rooted teeth.…”

Clorhexidina como alternativa para el acondicionamiento dentinario en la rehabilitación del diente endodónticamente tratado

“…6,[18][19][20][21][22][23][24][25][26] Estudios recientes proponen el uso de la Clorhexidina (CHX) para fortalecer la adhesión a la dentina radicular y superficial, ya que es una sustancia surfactante que mejora la calidad de la adhesión a la pared de la dentina radicular, así como un potente inhibidor enzimático de las metaloproteinasas (MPP) y catepsinas de cisteína [27][28][29] , evitando así, la degradación de las fibras colágenas y proteoglicanos que son fundamentales para que exista una capa híbrida y optimice el procedimiento adhesivo. [31][32][33] Por su parte, Dos Santos et al 34 y Gerhadt et al 35 sugieren que después de la desobturación para la rehabilitación con pernos de fibra de vidrio aplicar CHX 2% por 60seg, y luego secar la superficie dentinaria con puntas de papel absorbentes para posteriormente aplicar el sistema adhesivo autograbante, con la finalidad que la restauración del DET mantenga longevidad y función. 36 Por lo que el propósito de esta revisión es describir la importancia y beneficios del uso de la CHX para el acondicionamiento dentinario en la rehabilitación de dientes endodónticamente tratados.…”