Effects of calcium hydroxide addition on the physical and chemical properties of a calcium silicate-based sealer

Abstract

Recently, various calcium silicate-based sealers have been introduced for use in root canal filling. The MTA Fillapex is one of these sealers, but some of its physicochemical properties are not in accordance with the ISO requirements.ObjectiveThe aim of this study was to evaluate the flowability, pH level and calcium release of pure MTA Fillapex (MTAF) or containing 5% (MTAF5) or 10% (MTAF10) calcium hydroxide (CH), in weight, in comparison with AH Plus sealer.Material and MethodsThe flowability test was performed according to the ISO 6876:2001 requirements. For the pH level and calcium ion release analyses, the sealers were placed individually (n=10) in plastic tubes and immersed in deionized water. After 24 hours, 7 and 14 days, the water in which each specimen had been immersed was evaluated to determine the pH level changes and calcium released. Flowability, pH level and calcium release data were analyzed statistically by the ANOVA test (α=5%).ResultsIn relation to flowability: MTAF>AH Plus>MTAF5>MTAF10. In relation to the pH level, for 24 h: MTAF5=MTAF10=MTAF>AH Plus; for 7 and 14 days: MTAF5=MTAF10>MTAF>AH Plus. For the calcium release, for all periods: MTAF>MTAF5=MTAF10>AH Plus.ConclusionsThe addition of 5% CH to the MTA Fillapex (in weight) is an alternative to reduce the high flowability presented by the sealer, without interfering in its alkalization potential.

Determinação do pH e da liberação de íons cálcio de três cimentos endodônticos quando utilizados em obturações, em conjunto com guta-percha, e da qualidade das mesmas. Avaliação realizada em longo prazo

“…Em cultura de células, ele apresentou intenso efeito citotóxico (SCELZA et al, 2011;SILVA et al, 2013;YOSHINO et al, 2013) e genotóxico (BIN et al, 2012), principalmente nos períodos iniciais pós-manipulação (BIN et al, 2012 As propriedades físico-químicas e mecânicas do MTA Fillapex têm sido estudadas extensivamente. Os estudos têm mostrado que esse cimento apresenta uma alta solubilidade (BORGES et al, 2012;FARIA-JÚNIOR et al, 2013;VIAPIANA et al, 2014), propriedade esta que influencia positivamente na liberação de íons cálcio e hidroxila KUGA et al, 2014;ZHOU et al, 2013). No entanto, a alta solubilidade é indesejável, pois, a dissolução do cimento obturador gera a formação de gaps entre as paredes dentinárias e o material obturador, aumentando a possibilidade de infiltração bacteriana, com o tempo (ØRSTAVIK 2005).…”

“…No que se refere aos estudos in vitro, várias foram as formas descritas e utilizadas para a determinação do pH, como o uso do potenciômetro (TAMBURIC, VULETA, OGNJANOVIC, 1993), corante (STAEHLE et al, 1995) e peagômetro (ANTHONY; GORDON; DEL RIO, 1982;GORDON, ALEXANDER, 1886;TORABINEJAD et al, 1995;DEAL et al, 2002;DUARTE et al, 2003;DUARTE et al, 2004;FERREIRA et al, 2004;SANTOS et al, 2005;CHNG et al, 2005;YAP., 2006;ELDENIZ et al, 2007;BAE et al, 2011;TANOMARU-FILHO et al, 2011;MASSI et al, 2011;CANDEIRO et al, 2012;FARIA-JÚNIOR et al, 2013;SILVA et al, 2013;KUGA et al, 2014;VIAPIANA et al, 2014). A utilização de corantes como o vermelho cresol a 1%, utilizado por Staehle et al (1995), determina a ocorrência ou não da alcalinização pelo método visual, não fornecendo valores quantitativos.…”

“…O acondicionamento dos materiais em estudo em tubos de polietileno é um método bastante difundido na literatura para a determinação do pH e liberação de íons cálcio dos mesmos (DUARTE, 1996;DUARTE, 1999;BRANDÃO, 1999;DUARTE et al, 2000;DUARTE et al, 2003;DUARTE et al, 2004;FERREIRA et al, 2004;SANTOS et al, 2005;ELDENIZ 2007;TANOMARU-FILHO et al, 2009, BAE et al, 2011MASSI et al, 2011;CANDEIRO et al, 2012;SILVA et al, 2013;VIAPIANA et al, 2014;KUGA et al, 2014).…”

“…A determinação do pH foi realizada em períodos pré-estabelecidos, ou seja, 1 hora, 1 dia, 3 dias, 7 dias, 30 dias, 180 dias e 365 dias. Após cada período realizava-se a troca da água, fazendo com que cada material tivesse seu pH aferido somente em função do período avaliado, não havendo um somatório de valores (DUARTE et al, 2000;DUARTE et al, 2003;ELDENIZ et al, 2007;TANOMARU-FILHO et al, 2009, BAE et al, 2011MASSI et al, 2011;CANDEIRO et al, 2012;SILVA et al, 2013;VIAPIANA et al, 2014;KUGA et al, 2014). Quando da não renovação do líquido tem-se sempre uma ascendência dos valores, o que facilitaria a compreensão do desempenho dos materiais ao longo do tempo (ANTHONY; GORDON; DEL RIO, 1982;GORDON, ALEXANDER, 1986;FIDEL, 1993;FERREIRA et al, 2004).…”

“…O método mais empregado para determinação da quantidade de cálcio liberada consiste no acondicionamento do material em tubos de polietileno (DUARTE, 1996;DUARTE, 1999;BRANDÃO, 1999;DUARTE et al, 2000;DUARTE et al, 2003;DUARTE et al, 2004;FERREIRA et al, 2004;SANTOS et al, 2005;ELDENIZ 2007;TANOMARU-FILHO et al, 2010, BAE et al, 2011MASSI et al, 2011;CANDEIRO et al, 2012;SILVA et al, 2013;VIAPINA et al, 2014;KUGA et al, 2014), em dentes de acrílico HUNGARO DUARTE et al, 2012), ou em dentes extraídos (GORDON; ALEXANDER, 1986;STAEHLE et al, 1995;ESBERARD;CARNES;DEL RIO, 1996). No presente estudo dentes extraídos foram obturados pelas técnicas da condensação lateral e cone único com três diferentes cimentos.…”