Ataque de matrizes cimentícias por sulfato de sódio:adições minerais como agentes mitigadores

Filho, Juarez Hoppe; Souza, Diego Jesus de; Medeiros, Marcelo Henrique Farias de; Pereira, Eduardo; Portella, Kleber Franke

doi:10.1590/0366-69132015613581905

Cited by 21 publications

(11 citation statements)

References 17 publications

(19 reference statements)

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…No material cerâmico foi possível identificar um singelo halo amorfo característico de fração vítrea entre 15° e 40°, o que ocorreu entre 20° e 40° para o resíduo de concreto. No caso da cerâmica, este resultado indicou que o material apresentou uma baixa reatividade com a composição do cimento Portland, resultado também observado em [29]. O halo amorfo identificado no resíduo de concreto pode ser atribuído ao C-S-H da pasta de cimento hidratada, tendo em vista que este composto corresponde a uma formação amorfa.…”

Section: Resultsunclassified

“…O metacaulim é uma conhecida adição pozolânica de estrutura amorfa, obtido pela calcinação de argila caulinítica [33]. Os compostos identificados na DRX do material cerâmico são, excetuando-se o óxido de cálcio, os mesmos das pesquisas [29,34], que deu origem à adição pelo óxido [34]. A presença desta forma de metacaulim citada em [32] explicaria o comportamento desta adição nos outros ensaios de análise de reatividade pozolânica, pois o material teve interação com as argamassas e atingiu as resistências exigidas pela NBR 12653 [5].…”

Section: Resultsunclassified

See 1 more Smart Citation

Avaliação do potencial reativo de adições de resíduos de blocos de cerâmica vermelha e de concreto cominuído de RCD em matriz cimentícia

et al. 2019

Self Cite

View full text Add to dashboard Cite

Resumo Neste trabalho avaliou-se o potencial reativo de adições de resíduo de cerâmica vermelha (RCV) e de concreto de RCD, além de fíler calcário para referência. Avaliou-se o potencial pozolânico das adições por índice de atividade pozolânica (IAP) com cal, índice de desempenho (ID) com cimento, teor de hidróxido de cálcio fixado no Chapelle modificado e caracterização por difratometria de raios X (DRX). Os resultados mostram que o RCV atendeu aos requisitos químico-físicos para pozolanas, IAP com cal, ID com cimento e apresentou singelo halo amorfo na DRX indicando baixa reatividade, porém o material não atendeu requisitos mínimos no ensaio de Chapelle. O pó de concreto, apesar de não ser uma pozolana, foi submetido aos ensaios de IAP com cal e ID com cimento e apresentou resistências à compressão abaixo das mínimas prescritas nas normas pertinentes. Este material também apresentou halo amorfo na DRX, atribuído ao C-S-H da pasta de cimento hidratada.

show abstract

Section: Resultsunclassified

Avaliação do potencial reativo de adições de resíduos de blocos de cerâmica vermelha e de concreto cominuído de RCD em matriz cimentícia

et al. 2019

Self Cite

View full text Add to dashboard Cite

show abstract

“…Examples of those effects have been studied and are cited in the following studies: (a) Wang and Baxter [1] showed that the replacement of 25% of cement by fly ash has a similar compressive strength when compared to pure cement concrete at 1 and 12 months. (b) Hoppe Filho et al [2] showed that pozzolanic materials tend to reduce the expansion of the cementitious composites caused by sodium sulfate attack. (c) Choi et al [3] replaced 20% of Portland cement by fly ash (w/b ratios = 0.31, 0.35 and 0.50) showing that the use of fly ash has beneficial effects on the corrosion resistance of the steel in concrete due to the reduced permeability of chloride ions.…”

Section: Introductionmentioning

confidence: 99%

“…This study concluded that the hydration reaction, pozzolanic reaction, packing effect, and nucleation effect were enhanced by incorporating finer fly ashes. As a result, the paste with the finer fly ash has lower Ca(OH) 2 and becomes denser than the paste with the coarser fly ash. (f) Shehata and Thomas [6] showed that fly ash is most effective in reducing the alkalinity of the pore solution and also better for controlling ASR expansion.…”

Section: Introductionmentioning

confidence: 99%

Partial replacement and addition of fly ash in Portland cement: influences on carbonation and alkaline reserve

et al. 2017

View full text Add to dashboard Cite

This study aims to analyze the effect of using fly ash as a Portland cement additive or partial replacement in service conditions where carbonation acts as a degradation process. Fly ash was typified as anhydrous by XFR, XRD, modified Chapelle tests and laser granulometry. Five concretes were casted: one as reference (without additive), two with fly ash used as cement additive and two with fly ash used as a partial replacement of Portland cement. Replacement or additive levels were between 10 and 30% of cement mass. Those concretes were submitted to the compressive strength, accelerated carbonation and XRD tests using mortar extracted from the concrete in order to measure its alkaline supply. This researched allowed to conclude that alkaline reserve decreases and carbonation speed increases by adding or partially replacing the fly ash in the Portland cement. Besides, using fly ash reduces compressive strength at 28 days after wet cure. It is also important to highlight that there is an inverse correlation between alkaline reserve and carbonation speed in this case and, therefore, the remaining portlandite level is an important control factor in the carbonation process.

show abstract

“…Para tal é necessário que o concreto mantenha suas características e propriedades estabelecidas em projeto, frente as solicitações mecânicas e aos agentes agressivos presentes no ambiente ao qual está exposto, que podem levar a deteriorações do material no âmbito químico, físico e até biológico [1][2][3].…”

Section: Introductionunclassified

Efeito da adição de nanomagnetita (Fe3O4) em pastas de cimento Portland sujeitas ao ataque interno por sulfatos (ISA)

Pinkoski

Oliveira

Bragança

et al. 2017

Simpósio Paranaense De Patologia Das Construções

View full text Add to dashboard Cite

Resumo: A vida útil de estruturas de concreto utilizadas na construção civil deve sempre ser prolongada, independentemente do ambiente em que estão contidas, mantendo as suas características, quando submetidas as solicitações mecânicas e frente aos agentes agressivos. Com uma grande presença de agentes que possibilitam a ocorrência de degradação, torna-se carente a interface de recuperação e manutenção dessas estruturas. As adições surgem como uma proposta para melhorar as propriedades do concreto e minimizar os efeitos nocivos aos quais as obras estão sujeitas. Nesta ocasião, foram testados seis traços diferentes de pastas de cimento, com e sem contaminação por pirita, com a adição de nanomagnetita em diferentes teores (de 0,5% a 1,0%) pela técnica de microscopia eletrônica de varredura (MEV) e pelo ensaio de resistência à tração por compressão axial. Com o aumento do teor de nanomagnetita na mistura, foi possível verificar uma microestrutura mais densa assim como um incremento da resistência mecânica (de cerca de 50% aos 7 dias) e a mitigação dos efeitos de degradação causados pelo presença do sulfeto mineral.Palavras-chave: Pasta de cimento, Pirita, Sulfato, nano-Fe3O4. Abstract:The life cycle of concrete structures used on civil construction must be always extended, regardless of the environment in which they are contained, keeping their characteristics while maintaining its ones, when submitted to the mechanical requests and against the aggressive agents. With a large presence of agents that allow the occurrence of degradation, the retrieval and maintenance interface of these structures becomes lacking. The additions are a proposal to improve these properties of concrete and minimize the harmful effects to which the works are subject. At this occasion, different traces of cement paste were tested, with and without pyrite contamination, with the addition of nanomagnetite in different percentages by scanning electron microscopy (SEM) technique and tensile strength by axial compression test. By increasing nanomagnetite percentage in the mixture, it was possible to verify a denser microstructure, as well as an enhance of the mechanical resistance and the mitigation of the degradation effects caused by the contaminant.

show abstract

Ataque de matrizes cimentícias por sulfato de sódio:adições minerais como agentes mitigadores

Cited by 21 publications

References 17 publications

Avaliação do potencial reativo de adições de resíduos de blocos de cerâmica vermelha e de concreto cominuído de RCD em matriz cimentícia

Avaliação do potencial reativo de adições de resíduos de blocos de cerâmica vermelha e de concreto cominuído de RCD em matriz cimentícia

Partial replacement and addition of fly ash in Portland cement: influences on carbonation and alkaline reserve

Efeito da adição de nanomagnetita (Fe3O4) em pastas de cimento Portland sujeitas ao ataque interno por sulfatos (ISA)

Contact Info

Product

Resources

About