Eight different types of joining between two parallel high Tc superconducting (HTS) tapes were prepared and current-voltage ( -) characteristic curves were investigated at 77 K, liquid nitrogen temperature. Contact resistances of joint parts with 25 mm in length were estimated from -curves. Lowest contact resistance among eight samples having different types of joining was 0.497 . The best joining method is to do crossly joining with HTS tapes on two parallel HTS tapes after filling solder paste into their gap. In this case, lowest joint resistance was 0.15 at 77 K and 0.05 at 28 K. Joule heat of a joint sample generated at 30 K and at 100 A was calculated 0.492 mW. Also, in -curve of samples crossly joined with HTS tapes, it was found that joint resistance does not depend on variation of magnetic fields (0 7000 G) at 77 K. From consideration of Joule heat generation, such joining method is available for fabricating the field winding of superconducting rotating machine.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.