The electrical conductivity of undoped rutile ceramics is very dependent on sample processing conditions, especially the temperature and atmosphere during sintering and the subsequent cooling rate. Samples become increasingly semiconducting when quenched from temperatures above ~700°C without the need for a reducing atmosphere. Thus, samples quenched from 1400°C in air have conductivity ~1 × 10−2 Scm−1with activation energy ~0.01(1) eV over the temperature range 10–100 K, whereas similar samples that are slow cooled or annealed in air at 300°C–500°C are insulating with activation energy 1.67(2) eV and conductivity, e.g., 1 × 10−7 Scm−1 at 400°C. The very wide range of electrical properties is attributed to variations in oxygen content which are too small to be detected using thermogravimetry. Impedance analysis shows that, depending on cooling rate, partially oxidized samples may be prepared in which samples retain a semiconducting core, but have an oxidized outer layer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.