Nanoparticles of manganese antimonate (MnSb2O6) were prepared using the microwave-assisted colloidal method for its potential application as a gas sensor. For the synthesis of the oxide, manganese nitrate, antimony chloride, ethylenediamine and ethyl alcohol (as a solvent) were used. The precursor material was calcined at 800 °C in air and analyzed by X-ray diffraction. The oxide crystallized into a hexagonal structure with spatial group P321 and cell parameters a = b = 8.8054 Å and c = 4.7229 Å. The microstructure of the material was analyzed by scanning electron microscopy (SEM), finding the growth of microrods with a size of around ~10.27 μm and some other particles with an average size of ~1.3 μm. Photoacoustic spectroscopy (PAS) studies showed that the optical energy band (Eg) of the oxide was of ~1.79 eV. Transmission electron microscopy (TEM) analyses indicated that the size of the nanoparticles was of ~29.5 nm on average. The surface area of the powders was estimated at 14.6 m2/g by the Brunauer–Emmett–Teller (BET) method. Pellets prepared from the nanoparticles were tested in carbon monoxide (CO) and propane (C3H8) atmospheres at different concentrations (0–500 ppm) and operating temperatures (100, 200 and 300 °C). The pellets were very sensitive to changes in gas concentration and temperature: the response of the material rose as the concentration and temperature increased. The results showed that the MnSb2O6 nanoparticles can be a good candidate to be used as a novel gas sensor.
We have studied the Mg doping of cubic GaN grown by plasma-assisted Molecular Beam Epitaxy (PA-MBE) over GaAs (001) substrates. In particular, we concentrated on conditions to obtain heavy p-type doping to achieve low resistance films which can be used in bipolar devices. We simulated the Mg-doped GaN transport properties by density functional theory (DFT) to compare with the experimental data. Mg-doped GaN cubic epitaxial layers grown under optimized conditions show a free hole carrier concentration with a maximum value of 6 × 1019 cm−3 and mobility of 3 cm2/Vs. Deep level transient spectroscopy shows the presence of a trap with an activation energy of 114 meV presumably associated with nitrogen vacancies, which could be the cause for the observed self-compensation behavior in heavily Mg-doped GaN involving Mg-VN complexes. Furthermore, valence band analysis by X-ray photoelectron spectroscopy and photoluminescence spectroscopy revealed an Mg ionization energy of about 100 meV, which agrees quite well with the value of 99.6 meV obtained by DFT. Our results show that the cubic phase is a suitable alternative to generate a high free hole carrier concentration for GaN.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.