Here, we report for the first time a facile ultrasonic synthesis of Fe3O4 nanoparticles using FeCl3 and the organic solvent ethanolamine (ETA). The intermediate of the ETA-Fe(II) complex produces Fe3O4 after hydrolysis and hydrothermal treatment. The moderate reduction of ETA and ultrasound play an important role in the synthesis of superfine Fe3O4 particles with a very high specific surface area (165.05 m(2) g(-1)). The Fe3O4 nanoparticles were characterized by X-ray diffraction (XRD), scanning and transmission electron microscopy (SEM and TEM), high-resolution transmission electron microscopy (HRTEM), and ultraviolet-visible absorption spectroscopy (UV-vis). Fe3O4 as an electrode material was fabricated into a supercapacitor and characterized by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and galvanostatic charge-discharge measurements. The as-synthesized Fe3O4 exhibits remarkable pseudocapacitive activities including high specific capacitance (207.7 F g(-1) at 0.4 A g(-1)), good rate capability (90.4 F g(-1) at 10 A g(-1)), and excellent cycling stability (retention 100% after 2000 cycles). This novel synthetic route towards Fe3O4 is a convenient and potential way of producing a secondary energy material which is expected to be applicable in the synthesis of other metal oxide nanoparticles.

No abstract

No abstract

No abstract

The magnetic phase separation and exchange bias effect in off-stoichiometric Ni2Mn1.4Ga0.6 alloy were reported. Spontaneous exchange bias after zero-field cooling was observed in this alloy. The magnetic nature of ground state was characterized as phase separation with non-percolated ferromagnetic domains in spin glass matrix due to the spatial composition fluctuation and competing ferromagnetic and antiferromagnetic interactions. A mechanism of field-induced growth of ferromagnetic domains changing from non-percolating to percolating state was proposed for the appearance of spontaneous exchange bias.