The shear forces between poly(l-lysine)-graft-poly(ethylene glycol) (PLL-g-PEG)-modified SiO2 tribopairs have been measured with colloidal-probe, lateral force microscopy (LFM) and related to the mass of solvent absorbed within the brushlike structure of immobilized PEG chains. The amount of solvent (per unit substrate area) absorbed within the tethered, brushlike polymer, referred to as areal solvation, Ψ, appears to be of importance in determining the lubrication properties of the tethered polymers. In this study, the degree of solvation was varied by choosing different solvents (aqueous buffer solution, methanol, ethanol, and 2-propanol) and was determined by a technique that combines the results of quartz crystal microbalance (QCM-D) experiments and optical waveguide lightmode spectroscopy (OWLS). The highest degree of solvation was measured for aqueous buffer solutions, and a progressive decrease in solvation of PLL-g-PEG was observed in moving from methanol to ethanol to 2-propanol. A concomitant increase in the measured shear force was observed with this decrease in solvation. The lubrication mechanism of the PLL-g-PEG-coated SiO2 tribopair is discussed in terms of solvation and solvent quality and compared with the lubrication mechanism of the corresponding tribopair where only one surface is coated with the polymer brush.
We have investigated the collapse−stretching transition of a surface-bound, brushlike copolymer, poly(l-lysine)-graft-poly(ethylene glycol) (PLL-g-PEG), and the consequence of such transitions on the frictional properties of this coating. The frictional properties of the interface have been measured by colloidal-probe lateral force microscopy (LFM) in liquid environments on the nanoscale. The collapse−stretching transition has been induced through the systematic variation of the chemical composition of the binary solvent mixture comprised of an aqueous buffer solution and 2-propanol. The influence of solvent composition on the polymer conformation was monitored by comparing measurements conducted with optical waveguide lightmode spectroscopy (OWLS) and quartz crystal microbalance with dissipation monitoring (QCM-D). The combined approach employing QCM-D and OWLS has allowed the quantification of the mass of solvent molecules absorbed in the brushlike structure of PLL-g-PEG and has revealed a significant preferential solvation effect. This study has demonstrated preferential solvation of a surface-bound polymer and the role of such solvation in maintaining the favorable lubricating properties of a PEG brush when exposed to mixtures of good and poor solvents.
Reduction of the interfacial friction for the contact of a silicon oxide surface with sodium borosilicate in aqueous solutions has been accomplished through the adsorption of poly(L-lysine)-graft-poly(ethylene glycol) on one or both surfaces. Spontaneous polymer adsorption has been achieved via the electrostatic attraction of the cationic polylysine polymer backbone and a net negative surface charge, present for a specific range of solution pH values. Interfacial friction has been measured in aqueous solution, in the absence of wear, and on a microscopic scale with atomic force microscopy. The successful investigation of the polymer-coated interfaces has been aided by the use of sodium borosilicate microspheres (5.1 microm diameter) as the contacting probe tip. Measurements of interfacial friction as a function of applied load reveal a significant reduction in friction upon the adsorption of the polymer, as well as sensitivity to the coated nature of the interface (single-sided versus two-sided) and the composition of the adsorbed polymer. These measurements demonstrate the fundamental opportunity for lubrication in aqueous environments through the selective adsorption of polymer coatings.
The tribological properties of poly(L-lysine)-graft-poly(ethylene glycol) (PLL-g-PEG)-coated oxide interfaces have been investigated with atomic force microscopy (AFM) as a function of the molecular structure. Polymer-bearing surfaces were obtained via spontaneous adsorption of the polymer onto the oxide substrate from a buffered solution of physiological pH. Interfacial friction of these PLL-g-PEG-coated surfaces was found to be highly dependent on the duration of deposition and the architecture of PLL-g-PEG. In terms of the architecture, the PEG chain length and the grafting ratio (i.e., the molar ratio of L-lysine monomer to PEG side chain) of adsorbed PLL-g-PEG significantly influence the interfacial friction; specifically, friction is reduced as the PEG chain length increases and as the molar ratio of L-lysine monomer to PEG side chain decreases. The characteristics of the polymer deposition time and the influence of the lysine/PEG grafting ratio are rationalized in terms of spatial packing density considerations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.