Flexible graphene paper (GP) pillared by carbon black (CB) nanoparticles using a simple vacuum filtration method is developed as a high-performance electrode material for supercapacitors. Through the introduction of CB nanoparticles as spacers, the self-restacking of graphene sheets during the filtration process is mitigated to a great extent. The pillared GP-based supercapacitors exhibit excellent electrochemical performances and cyclic stabilities compared with GP without the addition of CB nanoparticles. At a scan rate of 10 mV s(-1) , the specific capacitance of the pillared GP is 138 F g(-1) and 83.2 F g(-1) with negligible 3.85% and 4.35% capacitance degradation after 2000 cycles in aqueous and organic electrolytes, respectively. At an extremely fast scan rate of 500 mV s (-1) , the specific capacitance can reach 80 F g(-1) in aqueous electrolyte. No binder is needed for assembling the supercapacitor cells and the pillared GP itself may serve as a current collector due to its intrinsic high electrical conductivity. The pillared GP has great potential in the development of promising flexible and ultralight-weight supercapacitors for electrochemical energy storage.
A Au-CeO(2) nanocomposite film has been investigated as a potential sensing element for high-temperature plasmonic sensing of H(2), CO, and NO(2) in an oxygen containing environment. The CeO(2) thin film was deposited by molecular beam epitaxy (MBE), and Au was implanted into the as-grown film at an elevated temperature followed by high temperature annealing to form well-defined Au nanoclusters. The Au-CeO(2) nanocomposite film was characterized by X-ray diffraction (XRD) and Rutherford backscattering spectrometry (RBS). For the gas sensing experiments, separate exposures to varying concentrations of H(2), CO, and NO(2) were performed at a temperature of 500 °C in oxygen backgrounds of 5.0, 10, and ∼21% O(2). Changes in the localized surface plasmon resonance (LSPR) absorption peak were monitored during gas exposures and are believed to be the result of oxidation-reduction processes that fill or create oxygen vacancies in the CeO(2). This process affects the LSPR peak position either by charge exchange with the Au nanoparticles (AuNPs) or by changes in the dielectric constant surrounding the particles. Spectral multivariate analysis was used to gauge the inherent selectivity of the film between the separate analytes. From principal component analysis (PCA), unique and identifiable responses were seen for each of the analytes. Linear discriminant analysis (LDA) was also used and showed separation between analytes as well as trends in gas concentration. Results indicate that the Au-CeO(2) thin film is selective to O(2), H(2), CO, and NO(2) in separate exposures. This, combined with the observed stability over long exposure periods, shows the Au-CeO(2) film has good potential as an optical sensing element for harsh environmental conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.