A superconducting diode is an electronic device that conducts supercurrent and exhibits zero resistance primarily for one direction of applied current. Such a dissipationless diode is a desirable unit for constructing electronic circuits with ultralow power consumption. However, realizing a superconducting diode is fundamentally and technologically challenging, as it usually requires a material structure without a centre of inversion, which is scarce among superconducting materials. Here, we demonstrate a superconducting diode achieved in a conventional superconducting film patterned with a conformal array of nanoscale holes, which breaks the spatial inversion symmetry. We showcase the superconducting diode effect through switchable and reversible rectification signals, which can be three orders of magnitude larger than that from a flux-quantum diode. The introduction of conformal potential landscapes for creating a superconducting diode is thereby proven as a convenient, tunable, yet vastly advantageous tool for superconducting electronics. This could be readily applicable to any superconducting materials, including cuprates and iron-based superconductors that have higher transition temperatures and are desirable in device applications.

We demonstrate direct evidence of possible surface superconductivity on small, well-shaped MgB2 single crystals. Transport measurements in the range H < 1.6H c c2 , where H c c2 is the bulk upper critical field for the c axis, show non-Ohmic and strongly angular dependent resistivity. Studies of the alignment of H with selected crystal surfaces, transport and specific heat measurements on the same crystal, and a physical sculpturing of the crystal surfaces using a focused ion beam all support the conclusion. Similar, albeit less pronounced results are obtained for fields in the basal plane.

No abstract

No abstract

YBa2Cu3O7-based coated conductors (CCs) achieve the highest critical current densities (J c) of any known superconductor and are a key technology for applications such as rotatory machines, high-field magnets and power transmission. Incorporation of nano-sized non-superconducting second phases as additional vortex pinning centers has been considered the most amenable route to further enhance J c at an industrial scale, and has been successfully used in commercial CCs. The resulting pinning landscape is quite complex, with both synergistic and competing interactions among the various types of defects. Particle irradiation, on the other hand, allows for a controlled post-processing incorporation of a well-defined defect morphology. We have previously shown that irradiation with protons and other light ions can further enhance the in-field J c in commercial state-of-the-art CCs. Here we develop a combined irradiation process that increases J c above values previously achieved by irradiating with only one species. Our new approach involves sequentially irradiating with 250 MeV Au ions and 4 MeV protons. For example, at T∼ 27 K (liquid neon) and µ 0 H∼ 4 T, a region of interest for rotatory machines applications, we obtain J c ∼ 5 MA cm−2, which is about 40% higher than the values produced by the individual irradiations. Finally, we conclude that this is due to the synergistic pinning effects of the introduced splayed, non-uniform columnar defects and small clusters.