Objectives:This study investigated the titratable acidity and erosive potential of acidic agents on the microhardness and surface micromorphology of four restorative materials.Methods:Forty-seven discs of each restorative material; metal-reinforced glass ionomer cement (Ketac-S), resin-modified glass ionomer cement (Fuji II LC), resin composite (Filtek Z250) and amalgam (Valiant-Ph.D.), 12 mm in diameter and 2.5 mm in thickness, were divided into four groups (5 discs/group). Specimens were then immersed for 7 days into four storage media; deionized water (control), citrate buffer solution, green mango juice and pineapple juice. Microhardness testing before and after immersions was performed. Micromorphological changes were evaluated under a scanning electron microscope (SEM). Statistical significance among each group was analyzed using two-way repeated ANOVA and Tukey’s tests.Results:The Fuji II LC and the Ketac-S showed the highest reduction in microhardness (P<.05). The Valiant-Ph.D. and the Filtek Z250 showed some minor changes over the period of 7 days. The mango juice produced the greatest degradation effect (P<.05).Conclusions:This study suggested that for restorations in patients who have tooth surface loss, materials selected should be considered. In terms of materials evaluated, amalgam and resin composite are the most suitable for restorations.
The acidic agents used in this study affected the microhardness and elemental dissolution of ceramics. The main elemental compositions of ceramics (silicon, aluminium and potassium) decreased after being immersed in acidic agents.
This study was conducted to evaluate the titratable acidity and effect of naturally acidic agents on the surface microhardness, elemental composition, and surface morphology of fluorapatite-leucite ceramics. One hundred and ten ceramic disks (IPS d.SIGN), 12.0 mm in diameter and 2.0 mm in thickness, were fabricated. Before immersion, the baseline data of Vickers microhardness and elemental composition were recorded. Four groups were immersed in acidic agents (citrate buffer solution, green mango juice, and pineapple juice) and deionized water (control) at 37ºC for 168 hours, whereas one group was immersed in 4% acetic acid at 80ºC for 168 hours. After immersion, specimens were evaluated and data were analyzed using one-way repeated ANOVA and Tukey's test (α=0.05). Microhardness values significantly decreased after immersion (p<0.05). In terms of elemental composition, the weight percentages of silicon, potassium, aluminum, and sodium also decreased after immersion (p<0.05). Results of this study showed that fluorapatite-leucite ceramics were affected by long-term immersion in acidic agents.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.