High-entropy oxides based on transition metals, such as Mg0.2Co0.2Ni0.2Cu0.2Zn0.2O (TM-HEO), have recently drawn special attention as potential anodes in lithium-ion batteries due to high specific capacity and cycling reversibility. However, the lithiation/delithiation mechanism of such systems is still controversial and not clearly addressed. Here, we report on an operando XAS investigation into TM-HEO-based anodes for lithium-ion cells during the first lithiation/delithiation cycle. This material showed a high specific capacity exceeding 600 mAh g–1 at 0.1 C and Coulombic efficiency very close to unity. The combination of functional and advanced spectroscopic studies revealed complex charging mechanisms, developing through the reduction of transition-metal (TM) cations, which triggers the conversion reaction below 1.0 V. The conversion is irreversible and incomplete, leading to the final collapse of the HEO rock-salt structure. Other redox processes are therefore discussed and called to account for the observed cycling behavior of the TM-HEO-based anode. Despite the irreversible phenomena, the HEO cubic structure remains intact for ∼60% of lithiation capacity, so proving the beneficial role of the configuration entropy in enhancing the stability of the HEO rock-salt structure during the redox phenomena.

No abstract

No abstract

The mechanisms of CO oxidation on the Mg 0.2 Co 0.2 Ni 0.2 Cu 0.2 Zn 0.2 O high-entropy oxide were studied by means of operando soft X-ray absorption spectroscopy. We found that Cu is the active metal and that Cu(II) can be rapidly reduced to Cu(I) by CO when the temperature is higher than 130 °C. Co and Ni do not have any role in this respect. The Cu(II) oxidation state can be easily but slowly recovered by treatment of the sample with O 2 at ca. 250 °C. However, it should be noted that CuO is readily and irreversibly reduced to Cu(I) when it is treated with CO at T > 100 °C. Thus, the main conclusion of this work is that the high configurational entropy of Mg 0.2 Co 0.2 Ni 0.2 Cu 0.2 Zn 0.2 O stabilizes the rock-salt structure and permits the oxidation/reduction of Cu to be reversible, thus permitting the catalytic cycle to take place.