The influences of process annealing temperature during cold rolling on microstructure and mechanical properties of Ti-3.5Al-5Mo-6V-3Cr-2Sn-0.5Fe near β high strength titanium alloy sheets have been investigated. Results showed that the alloy mainly included the deformation induced dislocation structures after cold rolling but no obvious band structure, twin crystal or martensite were observed in this work. The texture components, which were affected by process annealing, are mainly γ-fiber, α-fiber and weak Goss texture. The γ-fiber of alloy when process annealed at 780 °C (α/β phase field) is stronger than at 830 °C (β phase field), where the Goss texture of alloy with process annealing temperature of 830 °C is more obvious. Results of annealing heat treatments showed that the recrystallization of the cold rolled was basically completed in a relatively short time of 2 min at 750 °C for 2 min. The refinement of grain size led to a significant increase of plasticity compared to rolled alloy. Results of tensile testing of aged alloy display the excellent combination of strength and plasticity, and the cold rolled alloy with process annealed at α/β phase field exhibits the better mechanical properties than at β phase field.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.