The catalyst system i‐Pr(Cp)(9‐Flu)ZrCl2/methylaluminoxane was used for the synthesis of random syndiotactic copolymers of propylene with 1‐hexene, 1‐dodecene, and 1‐octadecene as comonomers. An investigation of the microstructure by 13C NMR spectroscopy revealed that the stereoregularity of the copolymers decreased because of an increase in skipped insertions in the presence of the higher 1‐olefin. The melting temperature of the copolymers, as measured by differential scanning calorimetry (DSC), decreased linearly with increasing comonomer content independently of the comonomer nature. During the DSC heating cycle, an exothermic peak indicating a crystallization process was observed. The decrease in the crystallization temperature with higher 1‐olefin content, measured by crystallization analysis fractionation, indicated a small but significant dependence on the nature of the comonomer. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 128–140, 2002

Ethylene - methyl methacrylate block copolymers are semicrystalline polymers that dissolve in organic solvents only at high temperatures. Accordingly, microstructure analysis by solution methods must be conducted at temperatures above 130°C. For the analysis of block copolymers of different compositions several analytical techniques were used, including high-temperature size-exclusion chromatography (SEC), hyphenated SEC-FTIR, and CRYSTAF (crystallisation analysis fractionation). While SEC with refractive index detection indicated a certain multimodality of the samples, SEC coupled with FTIR revealed that the samples were chemically inhomogeneous and may contain homo- and copolymer fractions. The presence of polyethylene and poly(methyl methacrylate) homopolymers in the copolymer samples was confirmed by CRYSTAF analysis, when the total concentration as well as the carbonyl group distribution were monitored separately. Chromatographic separation of the different sample components was achieved when liquid chromatography at critical conditions (LC-CC) was used. For the first time, true high-temperature LC-CC methods were developed operating at a column temperature of 140°C. As the stationary phase, silica gel was used. Suitable mobile phases were binary mixtures of 1,2,4-trichlorobenzene or 1,2- dichlorobenzene with cyclohexanone. Using LC-CC, the samples were separated into the copolymer and the homopolymer fractions.

Copolymers of ethylene with 1-decene, 1-tetradecene and 1-octadecene were prepared using the catalyst system racEt[Ind]2ZrCl2/MAO and were analysed with regard to chemical heterogeneity using crystallisation analysis fractionation (CRYSTAF), differential scanning calorimetry (DSC) and size exclusion chromatography coupled to FTIR (SEC-FTIR). The melting and crystallisation temperatures from DSC decrease linearly with increasing amount of comonomer, independently of the nature thereof. The decrease in crystallisation temperature from CRYSTAF of copolymers with higher 1-olefin content indicates a small dependence on the length of the side chain. The chemical heterogeneity of the copolymers as analysed by DSC and CRYSTAF broadens with increasing comonomer concentration.

ABSTRACT:The growing number of heterogeneous polymeric species that are being synthesized places increasing demands on existing analytical techniques. Although sizeexclusion chromatography (SEC) has established itself as a powerful analytical tool, it has its limits when complex polymers, e.g., graft copolymers, must be analyzed. In this case, complementary techniques such as gradient HPLC and liquid chromatography at critical conditions (LCCC) are more favorable. The present study describes the synthesis and analysis of methyl methacrylate-and styrene-grafted epoxidized natural rubber by different chromatographic techniques. The grafting efficiency was evaluated by gradient HPLC under normal and reversed phase conditions. Methyl methacrylate-grafted ENR50 was further analyzed by LCCC, where separation of the rubber and grafted rubber occurred according to chemical composition but was independent of the molar mass of the methyl methacrylate homopolymers. This was followed by the combination of LCCC and SEC, where separation was achieved in two dimensions. Relevant deductions were made of both the chemical composition distribution and the molar mass distribution of the functional groups of methyl methacrylategrafted ENR50.