Porous NiTi scaffolds display unique bone-like properties including low stiffness and superelastic behavior which makes them promising for biomedical applications. The present article focuses on the techniques to enhance superelasticity of porous NiTi structures. Selective Laser Melting (SLM) method was employed to fabricate the dense and porous (32-58%) NiTi parts. The fabricated samples were subsequently heat-treated (solution annealing + aging at 350 °C for 15 min) and their thermo-mechanical properties were determined as functions of temperature and stress. Additionally, the mechanical behaviors of the samples were simulated and compared to the experimental results. It is shown that SLM NiTi with up to 58% porosity can display shape memory effect with full recovery under 100 MPa nominal stress. Dense SLM NiTi could show almost perfect superelasticity with strain recovery of 5.65 after 6% deformation at body temperatures. The strain recoveries were 3.5, 3.6, and 2.7% for samples with porosity levels of 32%, 45%, and 58%, respectively. Furthermore, it was shown that Young's modulus (i.e., stiffness) of NiTi parts can be tuned by adjusting the porosity levels to match the properties of the bones.
Shape memory alloys (SMAs), such as Nitinol (i.e., NiTi), are of great importance in biomedical and engineering applications due to their unique superelasticity and shape memory properties. In recent years, additive manufacturing (AM) processes have been used to produce complex NiTi components, which provide the ability to tailor microstructure and thus the critical properties of the alloys, such as the superelastic behavior and transformation temperatures (TTs), by selection of processing parameters. In biomedical applications, superelasticity in implants play a critical role since it gives the implants bone-like behavior. In this study, a methodology of improving superelasticity in Ni-rich NiTi components without the need for any kind of post-process heat treatments will be revealed. It will be shown that superelasticity with 5.62% strain recovery and 98% recovery ratio can be observed in Ni-rich NiTi after the sample is processed with 250 W laser power, 1250 mm/s scanning speed, and 80 µm hatch spacing without, any post-process heat treatments. This superelasticity in as-fabricated Ni-rich SLM NiTi was not previously possible in the absence of post-process heat treatments. The findings of this study promise the fast, reliable and inexpensive fabrication of complex shaped superelastic NiTi components for many envisioned applications such as patient-specific biomedical implants.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.