SUMMARYCost and durability are central issues in the commercialization of proton-exchange membrane fuel cells. This study used complex accelerated-degradation protocols to diagnose the degradation modes of low-cost polytetrafluoroethylene-Nafion membrane electrode assemblies (MEAs). Acceleration protocols included open-circuit voltage, relative humidity cycling, and load cycling. Failure modes included measurements of cyclic voltammetry, linear sweep voltammetry, polarization curve, and AC impedance. The four modes (stages) of degradation were determined to be (i) catalyst aging, (ii) creep deformation, (iii) pinhole formation, and (iv) membrane failure. During catalyst aging, the maximum power density decreased by 0.117 mW cm À2 cycle À1 . After the 280th cycle, creep deformation occurred, and the maximum power density decreased by 0.227 mW cm À2 cycle
À1. Pinholes led to membrane failure and a final dramatic loss of performance (À0.453 mW cm À2 cycle À1 ). Therefore, membrane failure is the major factor in the failure of MEAs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.