Interaction between metal Fe and a variety of natural and synthetic smectite samples with contrasting crystal chemistry was studied by scanning electron microscopy and X-ray diffraction from experiments conducted at 80°C. These experiments demonstrate an important reactivity contrast as a function of smectite crystal chemistry. An XRD method involving the use of an internal standard allowed quantification of the relative proportion of smectite destabilized as a function of initial pH conditions as well as of smectite structural parameters. In mildly acidic to neutral pH conditions, a significant proportion of metal Fe is corroded to form magnetite without smectite destabilization. Under basic pH conditions, smectite and metal Fe are partly destabilized to form magnetite and newly-formed 1:1 phyllosilicate phases (odinite and crondstedtite). More specifically, systematic destabilization of both metal Fe and smectite is observed for dioctahedral smectites while trioctahedral smectites are essentially unaffected under similar experimental conditions. In addition, smectite reactivity is enhanced with increasing Fe3+ content and with the presence of Na+ cations in smectite interlayers. A conceptual model for smectite destabilization is proposed. This model involves first the release of protons from smectite structure, MeFe3+OH groups being deprotonated preferentially and metal Fe acting as proton acceptor. Corrosion of metal Fe results from its interaction with these protons. The Fe2+ cations resulting from this corrosion process sorb on the edges of smectite particles to induce the reduction of structural Fe3+ and migrate into smectite interlayers to compensate for the increased layer-charge deficit. Interlayer Fe2+ cations subsequently migrate to the octahedral sheet of smectite because of the extremely large layer-charge deficit. At low temperature, this migration is favored by the reaction time and by the absence of protons within the di-trigonal cavity. Smectite destabilization results from the inability of the tetrahedral sheets to accommodate the larger dimensions of the newly formed trioctahedral domains resulting from the migration of Fe2+ cations.
International audienceThe aim of this study is to synthesize and finely characterize montmorillonite samples, dioctahedral smectites without tetrahedral charges (structural formulae Nax(Al(2 − x)Mgx)Si4O10(OH)2), to allow their use as reference samples in clay science. The montmorillonites synthesis under hydrothermal conditions at different pressures and with various layer charge deficit has been attempted. The temperature was fixed at 320 °C, the pressure parameter values were 20 MPa, 80 MPa, 120 MPa and 200 MPa. The Mg content varied from 0.25 to 0.60 per half unit cell. The reaction products have been characterized with multi-technique analyses (ICP-AES, EMP, CEC, XRD, FTIR, NMR and TGA). Montmorillonite phase was only produced at 120 and 200 MPa. At 20 and 80 MPa, the results suggest that a 0.33 and 0.16-tetrahedral charge deficit exist in the formed samples. Moreover, the octahedral occupancies are higher than two (2.15 and 2.07 at 20 and 80 MPa respectively). In these experimental conditions, the synthetic smectites are mixtures between montmorillonite, beidellite and saponite. At 120 MPa and for a Mg content of 0.25 or higher than 0.33, the synthetic products were also mixtures of smectites. Tetrahedral charge deficits of 0.11, 0.11 and 0.15 were found for Mg contents of 0.25, 0.50 and 0.60 respectively. The octahedral occupancy was also higher than 2.00. A montmorillonite phase with only octahedral charges and an octahedral occupancy near 2.00 was synthesized for a Mg content of 0.33 and at pressures equal to or higher than 120 MPa. This low charge reference smectite shows a very low amount of accessory minerals and an octahedral charge deficit only created by the presence of magnesium in the structure. This montmorillonite can be compared structurally to the most studied natural one: the montmorillonite SWy-2 from Wyoming
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.