This work aimed to study the microstructure, wear and corrosion resistance of supermartensitic stainless steel (SMSS). Heat treatment applied to samples consists of quenching after austenitization at elevated temperature (1250 °C) followed by a double tempering at 650 °C. Conventional mechanical properties, scanning electron microscopy (SEM/EDS) analysis and X-ray diffraction methods (XRD) are used to analyze the microstructure and to evaluate the wear mechanisms. The potentiodynamic polarisation and the electrochemical impedance spectroscoopy (EIS) methods are used to evaluate the corrosion resistance in both the 0.5M H2SO4 and 0.5M NaCl aggressive media. The microstructure is mainly composed with tempered lath martensite, small quantity of retained austenite and carbides. Oxidative and abrasive wear dominated the wear process in dry condition. During the corrosion process, the same mechanism of degradation was found in both the 0.5M NaCl and 0.5M H2SO4.
Wear behavior of 13Cr5Ni2Mo supermartensitic stainless steel (SMSS) were investigated in air and in argillaceous paste at room temperature. Prior to wear testing, the samples were subjected to two thermal treatments, namely; quenching followed by double tempering. A pin-ondisc test rig was used to conduct the wear test with a tribo-pair consisting of supermartensitic stainless steel sliding against itself. It was observed that the microstructure of the thermally treated samples mainly consisted of tempered martensite and carbides. Wear results showed that oxidative and abrasive wear dominated the wear process of the treated samples in both dry conditions and in argillaceous paste. Additionally corrosion tests were performed in 5.0% NaCl solution via potentiodynamic polarization tests. It was found that the passive film formation provides a good corrosion resistance to the samples.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.