While surface acoustic wave (SAW) sensors have been used to measure temperature, pressure, strains, and low magnetic fields, the capability to measure bipolar fields and high fields is lacking. In this paper, we report magnetic surface acoustic wave sensors that consist of interdigital transducers made of a single magnetostrictive material, either Ni or TbFe 2 , or based on exchange-biased (Co=IrMn) multilayers. By controlling the ferromagnet magnetic properties, high-field sensors can be obtained with unipolar or bipolar responses. The issue of hysteretic response of the ferromagnetic material is especially addressed, and the control of the magnetic properties ensures the reversible behavior in the SAW response.

A study of the multilayer system MgO/CoFeB(1.1nm)/Ta(t)/CoFeB(0.8nm)/MgO is presented, where the two CoFeB layers are separated by a Ta interlayer of varying thickness t. The magnetization properties deduced from complementary techniques such as superconducting quantum interference magnetometry, ferromagnetic resonance frequency measurements and Brillouin light scattering spectroscopy can be tuned by changing the Ta thickness between t=0.25 nm, 0.5 nm and 0.75 nm. For t=0.5 nm, a ferromagnetic coupling is observed, whereas for t=0.75 nm, the antiferromagnetic coupling needed to construct a synthetic ferrimagnet is realized. In the later case, the shape of magnetic domain walls between two ferrimagnetic alignments or between a ferro-and a ferrimagnetic alignment is very different. This behavior can be interpreted as a result of the change in dipolar as well as interlayer exchange energy and domain wall pinning, which is an important conclusion for the realization of data storage devices based on synthetic ferri-and antiferromagnets.