AlFe2B2 was prepared by two alternative synthetic routes, arc melting and synthesis from Ga flux. In the layered crystal structure, infinite chains of B atoms are connected by Fe atoms into two-dimensional [Fe2B2] slabs that alternate with layers of Al atoms. As expected from the theoretical analysis of electronic band structure, the compound exhibits itinerant ferromagnetism, with the ordering temperature of 307 K. The measurement of magnetocaloric effect (MCE) as a function of applied magnetic field reveals isothermal entropy changes of 4.1 J kg(-1) K(-1) at 2 T and 7.7 J kg(-1) K(-1) at 5 T. These are the largest values observed near room temperature for any metal boride and for any magnetic material of the vast 122 family of layered structures. Importantly, AlFe2B2 represents a rare case of a lightweight material prepared from earth-abundant, benign reactants which exhibits a substantial MCE while not containing any rare-earth elements.

No abstract

Cobalt ferrite one-dimensional nanostructures (nanoribbons and nanofibers) were prepared by electrospinning combined with sol−gel technology. The nanoribbons and nanofibers were formed through assembling magnetic nanoparticles with poly(vinyl pyrrolidone) (PVP) as the structure-directing template. Nanoribbons and nanofibers were obtained after calcining the precursor nanoribbons at different temperatures. Successive Ostwald ripening processes occur during the formation of CoFe2O4 nanoribbons and nanofibers. The sizes of nanoparticles varied with calcination temperatures, which leads to different one-dimensional structures and variable magnetic properties. These novel magnetic one-dimensional structures can potentially be used in nanoelectronic devices, magnetic sensors, and flexible magnets.

Spinel ferrite, MFe 2O 4 (M = Co, Ni), ribbons with nanoporous structure were prepared by electrospinning combined with sol-gel technology. The ribbons were formed through the agglomeration of magnetic nanoparticles with PVP as the structure directing template. The length of the polycrystalline ribbons can reach millimeters, and the width of the ribbons can be tuned from several micrometers to several hundred nanometers by changing the concentration of precursor. The nanoporous structure was formed during the decomposition of PVP and inorganic salts. The ribbons exhibited weak saturation magnetizations and low coercivities at room temperature, but at low temperature, saturation magnetizations and coercivities increased a lot, especially for CoFe 2O 4 ribbons, reaching 72 emu/g and 1.45 T at 2 k, respectively. These novel magnetic ribbons can potentially be used in micro/nano electronic devices, gas-sensors, and catalysts.